Coated printing paper
The object of the present invention is to provide a coated printing paper used for ink jet printing machines, which has an ink fixing property and ink absorption property corresponding to ink jet printing, which inhibits poor dot diffusion, and which is excellent in abrasion resistance property of printed portions. According to the present invention, provided is a coated printing paper comprising a base paper, an undercoating layer which is applied on at least one surface of the base paper and contains a pigment and a binder, and one or more coating layers on the undercoating layer, wherein the base paper contains at least one selected from a cationic resin and a multivalent cation salt; the uppermost coating layer contains at least a colloidal silica; and the 75° gloss according to JIS Z8741 of the surface of the uppermost coating layer is 40% or more.
1. A coated printing paper comprising a base paper, an undercoating layer which is applied on at least one surface of the base paper and contains a pigment and a binder, and one or more coating layers on the undercoating layer, wherein
the base paper contains at least one selected from a cationic resin and a multivalent cation salt, and
an uppermost coating layer contains at least a colloidal silica, and a 75° gloss according to JIS Z8741 of a surface of the uppermost coating layer is 40% or more,
the colloidal silica contained in the uppermost coating layer includes a colloidal silica composite synthetic resin, and
the binder contained in the uppermost coating layer is a water dispersible binder, and a glass transition temperature of the water dispersible binder is lower than the glass transition temperature of the synthetic resin included in the colloidal silica composite synthetic resin,
wherein the coated printing paper is used for a printing machine employing ink jet recording system.
2. The coated printing paper according to claim 1 , wherein the base paper has a Cobb water absorption degree according to JIS P8140 of 60 g/m 2 or more at a contact time of 30 seconds.
3. The coated printing paper according to claim 1 , wherein a glass transition temperature of the synthetic resin included in the colloidal silica composite synthetic resin is 50° C. or more.
4. The coated printing paper according to claim 2 , wherein a glass transition temperature of the synthetic resin included in the colloidal silica composite synthetic resin is 50° C. or more.