Medical apparatus with lubricity and manufacturing method of same
The present disclosure provides a medical instrument with a coating that provides excellent lubricity when wet. The medical instrument possesses a coating including a wet lubricating film with high peel durability and anti-eluting properties. In embodiments, an intermediate film made of bisphenol A type epoxy resin is coated on a base material of a medical instrument made of metal, and a wet lubricant coating produced by alkaline processing of a polymer alloy containing a methyl vinyl ether maleic anhydride copolymer and a polyether block amide is then applied thereto. Methods for making these medical instruments are also provided.
1. A medical instrument comprising:
a base material comprising a metal;
an intermediate film covering a part of a surface of the base material, the intermediate film comprising a bisphenol A type epoxy resin; and
a wet lubricant formed on the intermediate film and on an exposed metal surface of the base material, the wet lubricant comprising a polymer alloy comprising a methyl vinyl ether maleic anhydride copolymer and a polyether block amide.
2. The medical instrument according to claim 1 , wherein the metal is selected from the group consisting of stainless steel, steel, copper, aluminum, and combinations thereof.
3. The medical instrument according to claim 1 , wherein the metal comprises stainless steel.
4. The medical instrument according to claim 1 , wherein the medical instrument is selected from the group consisting of guide wires, needles, and stylets.
5. The medical instrument according to claim 1 , wherein the medical instrument comprises a guide wire.
6. The medical instrument according to claim 1 , wherein the bisphenol A type epoxy resin is produced by reacting a bisphenol A epoxy resin prepolymer and a polyamide amine curing agent.
7. A method for forming a medical instrument comprising:
providing a base material comprising a metal;
forming an intermediate coating on at least an exposed metal surface of the base material by applying a solution containing bisphenol A type epoxy resin prepolymer and a polyamide amine-type curing agent in xylene and 1-butanol onto at least a part of the metal;
heating the bisphenol A type epoxy resin prepolymer and polyamide amine-type curing agent to form an intermediate film comprising a bisphenol A type epoxy resin;
applying to the intermediate film and on an exposed portion of the metal, a solution for forming a wet lubricant film comprising an acetone solution of methyl vinyl ether maleic anhydride copolymer and a tetrahydrofuran solution of a polyether block amide to form a polymer alloy comprising the methyl vinyl ether maleic anhydride copolymer and the polyether block amide; and
alkaline processing the polymer alloy to form a wet lubricant film.
8. The method according to claim 7 , wherein the metal is selected from the group consisting of stainless steel, steel, copper, aluminum, and combinations thereof.
9. The method according to claim 7 , wherein the metal comprises stainless steel.
10. The method according to claim 7 , wherein the medical instrument is selected from the group consisting of guide wires, needles, and stylets.
11. The method according to claim 7 , wherein the medical instrument comprises a guide wire.
12. The method according to claim 7 , wherein heating the bisphenol A type epoxy resin prepolymer and polyamide amine-type curing agent occurs at a temperature of from about 50° C. to about 100° C.
13. The method according to claim 7 , wherein heating the bisphenol A type epoxy resin prepolymer and polyamide amine-type curing agent occurs at a temperature of from about 70° C. to about 90° C.
14. The method according to claim 13 , wherein heating the bisphenol A type epoxy resin prepolymer and polyamide amine-type curing agent occurs for a period of time from about 2 hours to about 4 hours.
15. The method according to claim 7 , wherein the methyl vinyl ether maleic anhydride copolymer is present in the acetone solution at a concentration of from about 0.5 to about 5 percent by weight, and the polyether block amide is present in the tetrahydrofuran solution at a concentration of from about 0.5 to about 5 percent by weight.
16. The method according to claim 7 , wherein the ratio of the acetone solution of methyl vinyl ether maleic anhydride copolymer and the tetrahydrofuran solution of polyether block amide is at a weight ratio from about 10:1 to about 1:10.
17. The method according to claim 7 , wherein the ratio of the acetone solution of methyl vinyl ether maleic anhydride copolymer and the tetrahydrofuran solution of polyether block amide is at a weight ratio from about 3:1 to about 1:3.
18. The method according to claim 7 , wherein the wet lubricant film is dried at a temperature of from about room temperature to about 100° C.
19. The method according to claim 7 , wherein the wet lubricant film is dried at a temperature of from about 70° C. to about 90° C. for a period of time from about 2 hours to about 4 hours.
20. The method according to claim 7 , wherein alkaline processing the polymer alloy occurs by applying an aqueous solution of an alkali salt selected from the group consisting of sodium hydroxide, potassium hydroxide, and combinations thereof.
21. The method according to claim 20 , wherein the aqueous solution of an alkali salt is at a concentration from about 0.01 N to about 1 N.