Non-Pre-Colored Multi-Layer Zirconia Dental Blank that has a Gradual Change in Chroma through a Thickness After Sintering
A dental block for producing a dental prosthesis comprises a green body including zirconia and having a chemical composition including increasing amounts of yttria through a thickness of the green body. The green body is substantially white with a substantially consistent optical characteristic of chroma across the thickness, and is subsequently millable and sinterable to form the dental prosthesis with an optical characteristic of decreasing chroma through a thickness of the dental prosthesis.
1 . A dental block device for producing a dental prosthesis, the dental block device comprising:
a) a green body comprising zirconia;
b) the green body having multiple different layers each having a different chemical composition between adjacent layers;
c) the different chemical composition including different amounts of yttria between the adjacent layers;
d) the green body being substantially opaque and white with a substantially consistent optical characteristic of color intensity/chroma across the layers;
e) the green body having a brightness/lightness L* value between 10 to 20 for a sample thickness of 1 to 1.3 mm in accordance with CIE L*a*b* colorimetric system; and
f) the green body is subsequently millable, colorable and sinterable to form the dental prosthesis with the multiple different layers having different optical characteristics of color intensity/chroma.
2 . A device in accordance with claim 1 , wherein the amount of yttria is increased incrementally from a lower layer to an upper layer.
3 . A device in accordance with claim 2 , wherein the amount of yttria is increased incrementally from 4.5-6 wt % in the lower layer to 6-10 wt % in the upper layer.
4 . A device in accordance with claim 1 , wherein the multiple different layers have different thicknesses with respect to one another with a lower layer having a thickness between 2-5 mm and an upper layer having a thickness between 0.5-2 mm.
5 . A device in accordance with claim 1 , wherein the green body is without color pigment.
6 . A dental block device for producing a dental prosthesis, the dental block device comprising:
a) a green body comprising 60-99.9 wt % zirconia that is soft sintered or pre-sintered without color pigment;
b) the green body having multiple different layers each having a different chemical composition between adjacent layers and being substantially opaque and white with a substantially consistent optical characteristic of color intensity/chroma across the layers;
c) the different chemical composition including different amounts of yttria between adjacent layers with a lower layer having 4.5-6 wt % yttria and an upper layer having 6-10 wt % yttria;
d) the green body having a brightness/lightness L* value between 10 to 20 for a sample thickness of 1 to 1.3 mm in accordance with CIE L*a*b* colorimetric system; and
e) the green body is subsequently millable, colorable and sinterable to form the dental prosthesis with the multiple different layers having different optical characteristics of color intensity/chroma.
7 . A device in accordance with claim 6 , wherein the green body is millable to form a green dental prosthesis that is colorable and sinterable to form the dental prosthesis with the multiple different layers having different optical characteristics of color intensity/chroma after sintering.
8 . A device in accordance with claim 6 , wherein the multiple different layers have different thicknesses with respect to one another with the lower layer having a thickness between 2-5 mm and the upper layer having a thickness between 0.5-2 mm.
9 . A method for making a dental blank for use in producing a dental prosthesis, the method comprising:
a) forming zirconia and yttria into a desired shape;
b) increasing an amount of yttria through a thickness of the desired shape; and
c) pre-sintering or soft sintering the desired shape to form a green body dental blank with a different chemical composition of the amount of yttria through the thickness and being substantially opaque with a substantially consistent optical characteristic of color intensity/chroma across the thickness, the green body dental blank having a brightness/lightness L* value between 10 to 20 for a sample thickness of 1 to 1.3 mm in accordance with CIE L*a*b* colorimetric system.
10 . A method in accordance with claim 9 , wherein the amount of yttria is increased incrementally from 4.5-6 wt % in a lower portion to 6-10 wt % in an upper portion.
11 . A method in accordance with claim 9 , wherein forming zirconia and yttria into a desired shape and increasing the amount of yttria through a thickness of the desired shape further comprises:
a) combining zirconia with a first amount of yttria in a first mixture;
b) forming the first mixture into a first layer;
c) combining zirconia with a second different amount of yttria in at least a second mixture; and
d) disposing the at least the second mixture into a second layer on the first layer.
12 . A method in accordance with claim 11 , wherein the amount of yttria is increased incrementally from 4.5-6 wt % in a lower layer to 6-10 wt % in an upper layer.
13 . A method in accordance with claim 11 , wherein the layers have different thicknesses with respect to one another with a lower layer having a thickness between 2-5 mm and an upper layer having a thickness between 0.5-2 mm.
14 . A method in accordance with claim 9 , wherein the pre-sintering is done in the presence of atmospheric air.
15 . A method in accordance with claim 9 , wherein the zirconia powder and yttria are formed without color pigment.
16 . A method in accordance with claim 9 , further comprising:
a) milling a green body dental prosthesis from the green body dental blank;
b) coloring the green body dental prosthesis by dipping the green body dental prosthesis into a specific color liquid; and
c) sintering the green body dental prosthesis to form the dental prosthesis with an optical characteristic of decreasing color intensity/chroma across a thickness of the dental prosthesis after sintering.
17 . A method for making a dental a dental prosthesis, the method comprising:
a) obtaining a green body dental blank including zirconia and having multiple different layers each having a different chemical composition with different amounts of yttria between adjacent layers and being substantially opaque and white with a substantially consistent optical characteristic of color intensity/chroma across the layers, the green body dental blank having a brightness/lightness L* value between 10 to 20 for a sample thickness of 1 to 1.3 mm in accordance with CIE L*a*b* colorimetric system;
b) milling a green body dental prosthesis from the dental blank;
c) coloring the green body dental prosthesis by dipping the green body dental prosthesis into a specific color liquid;
d) sintering the green body dental prosthesis to form the dental prosthesis with the multiple different layers having different optical characteristics of color intensity/chroma after sintering.
18 . A method in accordance with claim 17 , wherein the sintering is done in the presence of atmospheric air.