Method of improving print performance in flexographic printing plates
View Patent ↗A method of making a relief image printing element from a photosensitive printing blank is provided. A photosensitive printing blank with a laser ablatable layer disposed on at least one photocurable layer is ablated with a laser to create an in situ mask. The printing blank is then exposed to at least one source of actinic radiation through the in situ mask to selectively cross link and cure portions of the photocurable layer. Diffusion of air into the at least one photocurable layer is limited during the exposing step and preferably at least one of the type, power and incident angle of illumination of the at least one source of actinic radiation is altered during the exposure step. The resulting relief image comprises a plurality of dots and a dot shape of the plurality of dots is produced that is highly resistant to print fluting for printing on corrugated board.
1. A method of making a relief image printing element from a photosensitive printing blank, said photosensitive printing blank comprising a laser ablatable layer disposed on at least one photocurable layer, the method comprising the steps of:
a) selectively laser ablating the laser ablatble layer to create an in situ mask and uncovering portions of the photocurable layer;
b) exposing the laser ablated printing blank to at least one source of actinic radiation through the in situ mask to selectively cross link and cure portions of the photocurable layer,
wherein the diffusion of air into the at least one photocurable layer is limited during the exposing step by a method selected from at least one of:
i) laminating a barrier membrane to the in situ mask and any uncovered portions of the photocurable layer bethre step (b); and
ii) coating the in situ mask and any uncovered portions of the photocurable layer with a layer of liquid prior to step (b);
wherein the oxygen diffusion coefficient of the barrier membrane and/or the layer of liquid is less than 6.9×10 −9 m 2 /sec.
2. The method according to claim 1 , wherein a barrier membrane is used and said barrier membrane comprises a material selected from the group consisting of polyamides, polyvinyl alcohol, hydroxyalkyl cellulose, copolymers of ethylene and vinyl acetate, amphoteric interpolymers, cellulose acetate butyrate, alkyl cellulose, butryal, cyclic rubbers, polypropylene, polyethylene, polyvinyl chloride, polyester and combinations of two or more of the foregoing.
3. The method according to claim 1 , wherein the barrier membrane is used and the barrier membrane comprises a surface with a defined surface roughness and wherein said defined surface roughness of the surface of the barrier membrane is impressed into the photocurable layer.
4. The method according to claim 3 , wherein the barrier membrane comprises a smooth surface with an average surface roughness of less than about 100 nm.
5. The method according to claim 1 , wherein the in situ mask and any uncovered portions of the photocurable layer are covered with a layer of oil prior to step (b).
6. The method according to claim 1 , wherein the barrier membrane is laminated to in situ mask and any uncovered portions of the photocurable layer using pressure and/or heat.
7. The method according to claim 1 , wherein the at least one of the type, power and incident angle of illumination of the at least one source of actinic radiation is altered during the exposure step.
8. The method according to claim 2 , wherein the at least one of the type, power and incident angle of illumination of the at least one source of actinic radiation is altered during the exposure step.
9. The method according to claim 2 , wherein the thickness of the barrier membrane is between about 1 and about 100 micron.
10. The method according to claim 9 , wherein the thickness of the barrier membrane is between about 1 and about 5 micron.
11. The method according to claim 2 , wherein the barrier membrane comprises a polypropylene film.
12. The method according to claim 3 , wherein the barrier membrane comprises a polyethylene terephthalate film with a cured photopolymer layer thereon.
13. The method according to claim 12 , wherein the cured photopolymer layer has a defined topographic pattern defined thereon and wherein the photopolymer layer is impressed into the surface of the photocurable layer during the lamination step.
14. The method according to claim 1 , further comprising the step of developing the photosensitive printing blank to reveal the relief image therein, by a method selected from the group consisting of water development, solvent development and thermal development.
15. A method according to claim 5 wherein the layer of oil is from 1 μm to 10 μm thick.
16. A method according to claim 3 wherein the barrier membrane has an optical transparency of at least 50 percent.
17. A method according to claim 15 wherein the layer of oil has an optical transparency of 50 percent.
18. A method according to any one of claims 1-17 wherein the oxygen diffusion coefficient is less than 6.9×10 −10 m 2 /sec.
19. A method of making a relief image printing element from a photosensitive printing blank, said photosensitive printing blank comprising a laser ablatable layer disposed on at least one photocurable layer, the method comprising the steps of:
a) selectively laser ablating the laser ablatable layer to create an in situ mask and uncovering portions of the photocurable layer;
b) exposing the laser ablated printing blank to at least one source of actinic radiation through the in situ mask to selectively cross link and cure portions of the photocurable layer,
wherein the diffusion of air into the at least one photocurable layer is limited during the exposing step by laminating a barrier membrane to the in situ mask and any uncovered portions of the photocurable layer before step (b);
wherein the oxygen diffusion coefficient of the barrier membrane is less than 6.9×10 −9 m 2 /sec.
20. The method according to claim 19 , wherein said barrier membrane comprises a material selected from the group consisting of polyamides, polyvinyl alcohol, hydroxyalkyl cellulose, copolymers of ethylene and vinyl acetate, amphoteric interpolymers, cellulose acetate butyrate, alkyl cellulose, butryal, cyclic rubbers, polypropylene, polyethylene, polyvinyl chloride, polyester and combinations of two or more of the foregoing.
21. The method according to claim 19 , wherein the barrier membrane comprises a surface with a defined surface roughness and wherein said defined surface roughness of the surface of the barrier membrane is impressed into the photocurable layer.
22. The method according to claim 21 , wherein the barrier membrane comprises a smooth surface with an average surface roughness of less than about 100μm.
23. The method according to claim 19 , wherein the barrier membrane is laminated to the situ mask and any uncovered portions of the photocurable layer using pressure and/or heat.
24. The method according to claim 19 , wherein the at least one of the type, power and incident angle of illumination of the at least one source of actinic radiation is altered during the exposure step.
25. The method according to claim 20 , wherein the at least one of the type, power and incident angle of illumination of the at least one source of actinic radiation is altered during the exposure step.
26. The method according to claim 20 , wherein the thickness of the barrier membrane is between about 1 and about 100 micron.
27. The method according to claim 26 , wherein the thickness of the barrier membrane is between about 1 and about 5 micron.
28. The method according to claim 20 , wherein the barrier membrane comprises a polypropylene film.
29. The method according to claim 21 , wherein the barrier membrane comprises a polyethylene terephthalate film with a cured photopolymer layer thereon.
30. The method according to claim 29 , wherein the cured photopolymer layer has a defined topographic pattern defined thereon and wherein the photopolymer layer is impressed into the surface of the photocurable layer during the lamination step.
31. The method according to claim 19 , further comprising the step of developing the photosensitive printing blank to reveal the relief image therein, by a method selected from the group consisting of water development, solvent development and thermal development.
32. A method according to claim 19 , wherein the barrier membrane has an optical transparency of at least 50 percent.
33. A method according to claim 19 , wherein the oxygen diffusion coefficient is less than 6.9×10 −10 m 2 /sec.