Process for the preparation of aqueous suspensions of anionic colloidal silica having a neutral PH and applications thereof
View Patent ↗The instant invention relates to a process for the preparation of an aqueous suspension of anionic colloidal silica having a neutral pH which is stable over time and comprises individualized particles of colloidal silica which are not bound to one another by siloxane bonds. The instant suspensions show high storage stability and are particularly useful for the clarification of beer, for the preparation of cosmetic formulations, for the production of ink for printers, for paints and for anticorrosive treatments.
1. A process for the preparation of inks, paints or anticorrosive treatments, comprising;
providing an aqueous suspension of anionic colloidal silica having a neutral pH, which is stable over time and comprising individualized particles of colloidal silica which are not bound to one another by siloxane bonds, where said aqueous suspension of anionic colloidal silica comprises individualized particles of colloidal silica which are not bound to one another by siloxane bonds and has a pH in the range from 8.5 to 11, a specific surface in the range from 20 m 2 /g to 700 m 2 /g, a mean particle diameter in the range from 4 nm to 150 nm and having a percentage of silica of ≧5 parts by weight, is reacted with an aqueous suspension of anionic colloidal silica comprising individualized particles of colloidal silica which are not bound to one another by siloxane bonds and having a pH in the range from 2 to 3.5, a specific surface in the range from 20 m 2 /g to 700 m 2 /g, a mean particle diameter in the range from 4 nm to 150 nm and having a percentage of silica of ≧5 parts by weight, further where the mean diameter of the particle is unchanged by the process;
providing a colored material; and,
forming a mixture of the colloidal silica with the colored material.
2. The process of claim 1 , where the aqueous suspension of anionic colloidal silica having a neutral pH is stable for greater than 6 months.
3. The process of claim 1 , where the aqueous suspension of anionic colloidal silica has a mean particle diameter in the range from 4 nm to 50 nm.
4. The process of claim 1 , where the preparation is an ink.
5. The process of claim 1 , where the preparation is a paint.
6. The process of claim 1 , where the preparation is an anticorrosive treatment.
7. The process of claim 4 , where said ink comprises a black T pigment.
8. The process of claim 4 , where said ink comprises an acid yellow pigment.
9. A method of application of the preparations obtained by the process according to claim 1 , wherein said application step is selected from the group consisting of painting or ink jet printing.