Method for manufacturing an extruded material of heat treatment type Al—Zn—Mg series aluminum alloy
A casted ingot of a heat treatment type Al—Zn—Mg series aluminum alloy comprising Zn: 4.0-8.0% by mass, Mg: 0.5-2.0% by mass, Cu: 0.05-0.5% by mass, Ti: 0.01-0.1% by mass, and any one or more of Mn: 0.1-0.7% by mass, Cr: 0.1-0.5% by mass and Zr: 0.05-0.3% by mass, and the balance being aluminum and incidental impurities is extruded at a homogenization treatment temperature after a homogenization treatment without cooled, and a resulted extruded material is die quenched at a cooling rate equal to or more than 100° C./min and then subjected to an artificial aging treatment, wherein the homogenization treatment is carried out by heating to the homogenization treatment temperature as 430-500° C. at a heating rate less than 750° C./hr or by heating to the homogenization treatment temperature and held the homogenization treatment temperature for 3 hours.
1. A method for manufacturing an extruded material of a heat treatment type Al—Zn—Mg series aluminum alloy, comprising:
(a) heating a casted ingot of a heat treatment type Al—Zn—Mg series aluminum alloy comprising Zn: 4.0-8.0% by mass, Mg: 0.5-2.0% by mass, Cu: 0.05-0.5% by mass, Ti: 0.01-0.1% by mass, and any one or more of Mn: 0.1-0.7% by mass, Cr: 0.1-0.5% by mass and Zr: 0.05-0.3% by mass, and the balance being aluminum and incidental impurities, to a homogenization treatment temperature at a heating rate of equal to or more than 70° C./hr and equal to or less than 750° C./hr;
(b) extruding the heated casting ingot from (a) at the homogenization treatment temperature;
(c) die quenching the extruded material from (b) at a cooling rate equal to or more than 100° C./min; and
(d) subjecting the die quenched material from (c) to an artificial aging treatment.
2. The method of claim 1 , wherein the homogenization treatment temperature is 430-500° C.
3. The method of claim 1 , wherein the extruded material from (b) is cooled to 50° C. or less in (c).