Red phosphor, method for producing red phosphor, white light source, illuminating device, and liquid crystal display device
A compound is provided containing silicon, aluminum, strontium, europium, nitrogen, and oxygen is used that enables a red phosphor having strong luminous intensity and high luminance to be obtained, and that enables the color gamut of a white LED to be increased with the use of the red phosphor. The red phosphor contains an element A, europium, silicon, aluminum, oxygen, and nitrogen at the atom number ratio of the following formula: [A (m−x) Eu x ]Si 9 Al y O n N [12+y−2(n−m)/3] . The element A in the formula is at least one of magnesium, calcium, strontium, and barium, and m, x, y, and n in the formula satisfy the relations 3<m<5, 0<x<1, 0<y<2, and 0<n<10.
1. A red phosphor comprising:
an element A, europium (Eu), silicon (Si), aluminum (Al), oxygen (O), and nitrogen (N) at the atom number ratio of the composition formula (1)
[A( m−x )Eu x ]Si 9 Al y O n N [12+y−2(n−m)/3] Composition Formula (1); and
Carbon,
wherein the amount of carbon ranges from about 0.05 to about 0.08 wt %, the element A in the composition formula (1) is at least one of magnesium (Mg), calcium (Ca), strontium (Sr), and barium (Ba), and m, x, y, and n in the composition formula (1) satisfy the relations 4.5<m<5, 0<x<1, 0<y<2, and 0<n<10, and wherein the compound of the composition formula (1) has a crystal structure that belongs to an orthorhombic system spatial point group Pmn2 1 .
2. The red phosphor according to claim 1 , wherein the carbon is produced through a mixing of a carbonate compound of element A and melamine, and heat treating the mixture to produce the carbon and hydrogen as the mixture undergoes pyrolysis.
3. The red phosphor according to claim 2 , wherein the amount of melamine in the mixture is 60 to 65 mol % relative to the amount of the carbonate compound of element A.
4. The red phosphor according to claim 2 , wherein at least a portion of the produced carbon is evaporated after binding to the oxygen atoms in the carbonate compound of element A to form a carbon oxide gas, the evaporation of the carbon oxide gas thereby reducing an amount of the oxygen in the red phosphor.
5. The red phosphor of claim 1 , wherein the element A is strontium (Sr).
6. A method for producing a red phosphor, the method comprising:
preparing a carbonate compound of an element A, europium nitride, silicon nitride, and aluminum nitride so as to contain the element A, europium (Eu), silicon (Si), and aluminum (Al) at the atom number ratio of the composition formula (1) below, and mixing melamine to produce a mixture including,
[A (m−x) Eu x ]Si 9 Al y O n N [12+y−2(n−m)/3] Composition Formula (1);
calcining the mixture to produce carbon; and
pulverizing a calcined product of the mixture,
wherein the amount of carbon in the mixture ranges from about 0.05 to about 0.08 wt %, the element A in the composition formula (1) is at least one of magnesium (Mg), calcium (Ca), strontium (Sr), and barium (Ba), and m, x, y, and n in the composition formula (1) satisfy the relations 4.5<m<5, 0<x<1, 0<y<2, and 0<n<10, and wherein the compound of the composition formula (1) has a crystal structure that belongs to an orthorhombic system spatial point group Pmn2 1 .
7. The method for producing a red phosphor according to claim 6 , wherein the calcining of the mixture produces the carbon and hydrogen as the mixture undergoes pyrolysis.
8. The method for producing a red phosphor according to claim 6 , wherein the amount of melamine is 60 to 65 mol % relative to the amount of the carbonate compound of element A.
9. The method for producing a red phosphor according to claim 6 , further comprising: forming carbon oxide gas through bonding of a portion of the produced carbon with oxygen atoms in the carbonate compound of element A; and evaporating at least a portion of the carbon oxide gas to reduce an amount of the oxygen in the red phosphor.
10. The method for producing a red phosphor of claim 6 , wherein the element A is strontium (Sr).
11. The method for producing the red phosphor of claim 6 , wherein the calcining of the mixture, and the pulverization of the calcined product of the mixture are repeated.