Fine grained Ni-based alloys for resistance to stress corrosion cracking and methods for their design
A class of nickel based alloys having a fine grain structure resistant to stress corrosion cracking, and methods of alloy design to produce further alloys within the class are presented. The alloys act as suitable welding materials in similar applications to that of Alloy 622. The fine-grained structure of these novel alloys may also be advantageous for other reasons as well such as wear, impact, abrasion, corrosion, etc. These alloys have similar phases to Alloy 622 in that they are composed primarily of austenitic nickel, however the phase morphology is a much finer grained structure opposed to the long dendritic grains common to Alloy 622 when it is subject to cooling rates from a liquid state inherent to the welding process.
1. A composition of matter, comprising:
a balance of nickel;
between approximately 25 and 30 wt. % chromium;
between approximately 10 and 15.5 wt. % molybdenum;
between approximately 0.3 and 1.6 wt. % boron; and
between 0 and approximately 3.5 wt. % silicon;
the composition not including titanium, niobium, tin, or iron except as an impurity.
2. The composition of claim 1 , further comprising:
a balance of nickel;
between approximately 26 and 29 wt. % chromium;
between approximately 10 and 15.5 wt. % molybdenum;
between approximately 0.4 and 1.2 wt. % boron; and
between approximately 1 and 3 wt. % silicon.
3. The composition of claim 1 , wherein the composition is in the form of an alloy.
4. The composition of claim 1 , wherein the composition is a component of a weld bead, the weld bead further comprising a substrate dilution component.
5. The composition of claim 1 , wherein the composition is a component of a weld overlay coating, the weld overlay coating further comprising a substrate dilution component.
6. The composition of claim 1 , wherein the composition is in the form of a welding wire.
7. The composition of claim 6 , wherein the welding wire is a cored welding wire comprising:
a sheath comprising nickel; and
a powder material disposed within the sheath; and
wherein melting of the cored welding wire during welding results in a weld pool having a composition comprising a dilution component and a weld component, the weld component comprising a balance of nickel, between approximately 25 and 30 wt. % chromium, between approximately 10 and 15.5 wt. % molybdenum, between approximately 0.3 and 1.6 wt. % boron, and between 0 and approximately 3.5 wt. % silicon, the composition not including titanium, niobium, tin, or iron except as an impurity.
8. The composition of claim 7 , wherein the sheath has a melting temperature that is at least 50° C. less than a melting temperature of a weld bead formed by solidification of the weld pool.
9. The composition of claim 1 , wherein the composition is configured such that an alloy formed from the composition possess phase morphologies of approximately 150 microns or less in the longest dimension when cooled from a liquid state at 5,000° K./s or less.
10. A composition of matter, comprising a mixture of one or more of:
Ni Bal Cr 27.35 Mo 10.71 Fe 0.23 Si 2.71 B 1.17 ;
Ni Bal Cr 28.86 Mo 15.17 Fe 0.14 Si 1.13 B 0.47 ;
Ni Bal Cr 26.7 Mo 12.7 Si 1.0 B 0.4 ; or
Ni Bal Cr 25.78 Mo 5.65 B 0.69 C 0.02 .
11. The composition of claim 9 , wherein the alloy has a microstructure form of at least 90% austenitic nickel.
12. The composition of claim 11 , wherein the microstructure further comprises silicide, boride, carbide, aluminide, or nitride precipitates.