Medical drill
A medical drill is disclosed, which is made of amorphous alloy, the amorphous alloy is zirconium amorphous alloy comprising 45 at % or above of zirconium, wherein the tensile strength of the medical drill is 1500-2500 Mpa, and the Vicker's hardness of the medical drill is 400-750. Moreover, a medical drill made of titanium amorphous alloy is also disclosed.
1. A medical drill made of an amorphous alloy, wherein the amorphous alloy is a Zr-based amorphous alloy which comprises zirconium metal in 45 at % or more, and the medical drill has a tensile strength of 1500-2500 MPa and a Vickers hardness of 400-750;
wherein the Zr-based amorphous alloy comprises zirconium in 45 at % or more, aluminum in 5-10 at %, copper in 15-20 at % and nickel in 5-15 at %, and further comprises silicon, boron, yttrium, palladium or tantalum in 1 at % or more;
wherein the Zr-based amorphous alloy is represented by the following formula of Zr 61 Al 7.5 Cu 17.5 Ni 10 B 2 .
2. The medical drill as claimed in claim 1 , wherein the medical drill is shaped in a pillar body, and a spiral structure is formed in a portion of the pillar body.
3. The medical drill as claimed in claim 1 , wherein the medical drill is shaped in a pillar body, and a thread is formed in a portion of the pillar body.
4. The medical drill as claimed in claim 1 , wherein the medical drill is manufactured by:
a) preparing an amorphous alloy rod through rapid cooling;
b) forming a spiral structure in a portion of the amorphous alloy rod by heating; and
c) a stretching and twisting process;
wherein a temperature of step (b) is not higher than a crystallization temperature (Tx) of the amorphous alloy.
5. A medical drill made of an amorphous alloy, wherein the amorphous alloy is a Zr-based amorphous alloy which comprises zirconium metal in 45 at % or more, and the medical drill has a tensile strength of 1500-2500 MPa and a Vickers hardness of 400-750;
wherein the Zr-based amorphous alloy comprises zirconium in 45 at % or more, aluminum in 5-10 at %, copper in 15-20 at % and nickel in 5-15 at %, and further comprises silicon, boron, yttrium, palladium or tantalum in 1 at % or more;
wherein the Zr-based amorphous alloy is represented by the following formula of Zr 53 Cu 30-x Ni 9 Al 8 Ta x therewith 0.1=<x=<10.
6. The medical drill as claimed in claim 5 , wherein the medical drill is manufactured by:
a) preparing an amorphous alloy rod through rapid cooling;
b) forming a spiral structure in a portion of the amorphous alloy rod by heating; and
c) a stretching and twisting process;
wherein a temperature of step (b) is not higher than a crystallization temperature (Tx) of the amorphous alloy.
7. A medical drill made of an amorphous alloy, wherein the amorphous alloy is a Zr-based amorphous alloy which comprises zirconium metal in 45 at % or more, and the medical drill has a tensile strength of 1500-2500 MPa and a Vickers hardness of 400-750;
wherein the Zr-based amorphous alloy comprises zirconium in 45 at % or more, aluminum in 5-10 at %, copper in 15-20 at % and nickel in 5-15 at %, and further comprises silicon, boron, yttrium, palladium or tantalum in 1 at % or more;
wherein the Zr-based amorphous alloy is represented by the following formula of Zr 53 Al 8 Cu 30 Pd x Nb y therewith x=4.5 and y=4.5.
8. The medical drill as claimed in claim 7 , wherein the medical drill is manufactured by:
a) preparing an amorphous alloy rod through rapid cooling;
b) forming a spiral structure in a portion of the amorphous alloy rod by heating; and
c) a stretching and twisting process;
wherein a temperature of step (b) is not higher than a crystallization temperature (Tx) of the amorphous alloy.