Electrode forming process for metal-ion battery with hexacyanometallate electrode

1. A method for forming a metal-ion battery electrode with large interstitial spacing, the method comprising:

forming a working electrode with hexacyanometallate particles overlying a current collector, the hexacyanometallate particles having a chemical formula A m M1 x M2 y (CN) 6 .zH 2 O, and having a Prussian Blue hexacyanometallate crystal structure,

where A is selected from a group consisting of alkali and alkaline-earth cations;

where M1 is a metal selected from a group consisting of 2+ and 3+ valance positions;

where M2 is a metal selected from a group consisting of 2+ and 3+ valance positions;

where m is in a range of 0 to 2;

where x is in a range of 0.5 to 1.5;

where y is in a range of 0.5 to 1.5;

where z is in a range of 0 to 10;

soaking the working electrode in an organic first electrolyte including a salt selected from the group consisting of alkali and alkaline earth cations;

accepting a first electric field in the first electrolyte between the working electrode and a first counter electrode;

in response to the first electric field, simultaneously removing A cations and water molecules from interstitial spaces in the Prussian Blue hexacyanometallate crystal structure;

forming hexacyanometallate particles having a chemical formula of A m′ M1 x M2 y (CN) 6 .z′H 2 O, where m′<m and z′<z, overlying the working electrode;

subsequent to forming A m′ M1 x M2 y (CN) 6 .zH 2 O, soaking the working electrode in an organic second electrolyte including a salt with A′ cations, where A′ is selected from a group consisting of alkali and alkaline-earth cations;

accepting a second electric field in the second electrolyte between the working electrode and a second counter electrode including A′ elements;

in response to the second electric field, adding A′ cations into the interstitial spaces of the A m′ M1 x M2 y (CN) 6 .zH 2 O crystal structure; and,

forming hexacyanometallate particles with the chemical formula A′ n A m′ M1 x M2 y (CN) 6 .z′H 2 O the metal current collector, where n is in a range of 0.5 to 2.

2. The method of claim 1 wherein soaking the working electrode in the second electrolyte including a salt with A′ cations includes the A′ cations being selected from a group consisting the same material as the A cations and a different material other than the A cations.

3. The method of claim 1 wherein forming hexacyanometallate particles having the chemical formula of A m′ M1 x M2 y (CN) 6 .z′H 2 O includes forming hexacyanometallate particles having the chemical formula of M1 x M2 y (CN) 6 , where m′=z=0.

4. The method of claim 1 wherein the A cations are selected from a group consisting of Na + , K + , Mg 2+ , and Ca 2+ .

5. The method of claim 1 wherein the A′ cations are selected from a group consisting of Na + , K + , Mg 2+ , and Ca 2+ .

6. The method of claim 1 wherein simultaneously removing A cations and water molecules from interstitial spaces in the Prussian Blue hexacyanometallate crystal structure in response to the first electric field includes forming a solid-electrolyte interphase (SEI) layer overlying the working electrode.

7. The method of claim 1 wherein soaking the working electrode in an organic second electrolyte, and accepting the second electric field in the second electrolyte between the working electrode and the second counter electrode includes soaking the working electrode in an assembled battery, where the second counter electrode is selected from a group consisting of an anode and a cathode, the working electrode is unselected from the group, and the second electric field inserts A′ cations into the interstitial spaces of the A m′ M1 x M2 y (CN) 6 .z′H 2 O crystal structure.