Polyolefin based hot melt containing a solid plasticizer
A hot melt adhesive that is composed of a metallocene catalyzed polyethylene polymer, a hydrogenated styrenic block copolymer, a tackifying resin, and a solid plasticizer. The preferred polyethylene polymer is an ethylene-octene copolymer, and the preferred styrenic block copolymer is a styrene-ethylene-butylene-styrene having less than 30% styrene content. The preferred solid plasticizer is either glycerol tribenzoate or 1,4-cyclohexane dimethanol dibenzoate.
1. A hot melt adhesive composition, comprising:
(a) about 40% to 60% by weight of a metallocene catalyzed polyolefin polymer, said polyolefin polymer is a polyethylene polymer, and said polyethylene polymer is a copolymer of ethylene and octene-1 having a melt index equal to or greater than 500 g/10 min;
(b) about 30% to 60% by weight of a tackifying resin having a softening point equal to or greater than 90° C.;
(c) about 2% to 12% by weight of a styrenic block copolymer, said styrenic block copolymer is a styrene-ethylene-butylene-styrene (SEBS) block copolymer having a styrene content of about 10% to about 13% by weight;
(d) about 2% to 15% by weight of a solid plasticizer having a softening point equal to or greater than 45° C.; and
wherein the composition has a storage modulus G 1 at 30° C. of at least 1×10 6 dynes/cm 2 , has a ratio of storage modulus G 1 at 30° C. to storage modulus G 1 at 70° C. equal to or greater than 100, is non-tacky when cool, and does not contain a wax.
2. The composition of claim 1 wherein said tackifying resin is selected from the group consisting of aliphatic and cyclo-aliphatic petroleum hydrocarbon resins, hydrogenated aliphatic and cyclo-aliphatic petroleum hydrocarbon resins, hydrogenated aromatic petroleum hydrocarbon resins, aliphatic/aromatic petroleum derived hydrocarbon resins, hydrogenated aliphatic/aromatic derived hydrocarbon resins, aromatic modified cyclo-aliphatic resins, hydrogenated aromatic modified cyclo-aliphatic resins, polyterpene resins, copolymers and terpolymers of natural terpenes, and mixtures thereof.
3. The composition of claim 1 wherein said styrenic block copolymer has a styrene content of about 13% by weight.
4. The composition of claim 1 having a viscosity of about 20,000 centipoise or less.
5. The composition of claim 1 having a viscosity of about 15,000 centipoise or less.
6. The composition of claim 1 having a viscosity of about 10,000 centipoise or less.
7. The composition of claim 1 having a ratio of storage modulus G 1 at 30° C. to storage modulus G 1 at 70° C. equal to or greater than 200.
8. The composition of claim 1 having a ratio of storage modulus G 1 at 30° C. to storage modulus G 1 at 70° C. equal to or greater than 500.
9. The composition of claim 1 wherein said solid plasticizer has a softening point equal to or greater than 60° C.
10. The composition of claim 9 wherein said solid plasticizer is selected from the group consisting of glycerol tribenzoate and 1,4-cyclohexane dimethanol dibenzoate.