Biodegradable aliphatic polyester particles and production process thereof
Biodegradable aliphatic polyester particles have: (A) an average particle diameter of 10 to 500 μm, and (B) a quantity of heat of low-temperature crystallization calculated as an exotherm attending on crystallization, detected in the course of heating by DSC, of at least 1 J/g, and preferably: (C) a quantity of heat of crystal melting calculated as an endotherm attending on melting of a crystal, detected in the course of the heating, of less than 100 J/g, and (D) a difference between the quantity of heat of crystal melting and the quantity of heat of low-temperature crystallization of less than 90 J/g. A process for producing the particles comprises grinding a particular biodegradable aliphatic polyester having a weight average molecular weight of at least 50,000 at not lower than 0° C. and lower than the glass transition temperature of the polyester while applying high shearing force.
1. Biodegradable aliphatic polyester particles, wherein the particles are soluble in an organic solvent at a temperature of 40° C. or lower and wherein:
(A) a biodegradable aliphatic polyester contained in the biodegradable aliphatic polyester particles is a polyglycolic acid having a weight average molecular weight of from 150,000 to 1,000,000,
(B) the average particle diameter (50% D) of the particles is 10 to 500 μm,
(C) the quantity of heat of low-temperature crystallization thereof as calculated out as an exotherm attending on crystallization, which is detected in the course of heating by a differential scanning calorimeter, is at least 1 J/g,
(D) the quantity of heat of crystal melting thereof as calculated out as an endotherm attending on melting of a crystal, which is detected in the course of heating by the differential scanning calorimeter, is less than 100 J/g,
(E) the biodegradable aliphatic polyester particles can be dissolved at a concentration of at least 2% by mass in an organic solvent at a temperature not higher than the glass transition temperature (Tg) of the biodegradable aliphatic polyester contained in the biodegradable aliphatic polyester particles−5° C., to prepare a solution, and
(F) solution viscosity is within a range of from 10 to 1,000 mPa·s, wherein the solution viscosity is determined by pouring 2 g of the biodegradable aliphatic polyester particles into 20 ml of hexafluoroisopropanol, stirring the resultant mixture for 2 hours while keeping the temperature of the system at 25° C., thereby preparing a solution, and conducting measurement on the solution at a temperature of 25° C. and a shear rate of 20 sec −1 .
2. The biodegradable aliphatic polyester particles according to claim 1 , wherein the organic solvent is at least one solvent selected from the group consisting of ester solvent, dibasic acid ester solvent, ketone solvent, hydrocarbon solvent, halogen-containing solvent, alcohol solvent, ether solvent, amide solvent, and pyrrolidone solvent.
3. The biodegradable aliphatic polyester particles according to claim 1 , wherein the average particle diameter thereof is 12 to 450 μm.
4. The biodegradable aliphatic polyester particles according to claim 1 , wherein the average particle diameter thereof is 20 to 300 μm.
5. The biodegradable aliphatic polyester particles according to claim 1 , wherein the average particle diameter thereof is 30 to 200 μm.
6. The biodegradable aliphatic polyester particles according to claim 1 , wherein the particles are soluble in an organic solvent at a temperature of 35° C. or lower.
7. The biodegradable aliphatic polyester particles according to claim 1 , wherein the particles are soluble in an organic solvent at a temperature of 30° C. or lower.
8. The biodegradable aliphatic polyester particles according to claim 1 , wherein the particles are soluble in an organic solvent at a temperature of 20 to 25° C.
9. The biodegradable aliphatic polyester particles according to claim 1 , wherein the particles can be dissolved at a concentration of at least 3% by mass in an organic solvent at a temperature not higher than the glass transition temperature (Tg) of the biodegradable aliphatic polyester contained in the biodegradable aliphatic polyester particles−5° C., to prepare a solution.
10. The biodegradable aliphatic polyester particles according to claim 1 , wherein the particles can be dissolved at a concentration of at least 4% by mass in an organic solvent at a temperature not higher than the glass transition temperature (Tg) of the biodegradable aliphatic polyester contained in the biodegradable aliphatic polyester particles−5° C., to prepare a solution.
11. The biodegradable aliphatic polyester particles according to claim 1 , wherein the particles can be dissolved at a concentration of at least 5% by mass in an organic solvent at a temperature not higher than the glass transition temperature (Tg) of the biodegradable aliphatic polyester contained in the biodegradable aliphatic polyester particles−5° C., to prepare a solution.
12. The biodegradable aliphatic polyester particles according to claim 1 , wherein the solution viscosity is within a range of from 50 to 800 mPa·s.
13. The biodegradable aliphatic polyester particles according to claim 1 , wherein the solution viscosity is within a range of from 100 to 600 mPa·s.
14. The biodegradable aliphatic polyester particles according to claim 1 , wherein the solution viscosity is within a range of from 150 to 500 mPa·s.
15. The biodegradable aliphatic polyester particles according to claim 1 , wherein (G) a difference between the quantity of heat of crystal melting and the quantity of heat of low-temperature crystallization is less than 90 J/g.
16. A process for producing the biodegradable aliphatic polyester particles according to claim 1 , which comprises grinding a particular biodegradable aliphatic polyester containing a polyglycolic acid at a temperature not lower than 0° C. and lower than the glass transition temperature of the biodegradable aliphatic polyester while applying high shearing force.