Hybrid nanoparticle TFC membranes
A process for preparing a reverse osmosis membrane that includes (A) providing a polyamine, a polyfunctional acid halide, and mono-hydrolyzed trimesoyl chloride; (B) combining the polyamine, polyfunctional acid halide, and mono-hydrolyzed trimesoyl chloride on the surface of a porous support membrane; and (C) interfacially polymerizing the polyamine and the polyfunctional acyl halide on the surface of the porous support membrane to form a reverse osmosis membrane comprising (i) the porous support membrane and (ii) a discrimination layer comprising a polyamide. The reverse osmosis membrane is characterized by a flux that is greater than the flux of the same membrane prepared in the absence of the mono-hydrolyzed trimesoyl chloride.
1. A process for preparing a reverse osmosis membrane, comprising:
(A) providing a polyamine, a polyfunctional acid halide, mono-hydrolyzed trimesoyl chloride, and nanoparticles;
(B) combining the polyamine, polyfunctional acid halide, mono-hydrolyzed trimesoyl chloride, and nanoparticles on the surface of a porous support membrane; and
(C) interfacially polymerizing the polyamine and the polyfunctional acid halide on the surface of the porous support membrane to form a reverse osmosis membrane comprising (i) the porous support membrane and (ii) a discrimination layer comprising a polyamide and the nanoparticles,
wherein the reverse osmosis membrane is characterized by a flux that is greater than the flux of the same membrane prepared in the absence of the mono-hydrolyzed trimesoyl chloride.
2. A process according to claim 1 wherein the polyamine is selected from the group consisting of diaminobenzene, triaminobenzene, m-phenylene diamine, p-phenylene diamine, 1,3,5-diaminobenzoic acid, 2,4-diaminotoluene, 2,4-diaminoanisole, xylylene-diamine, ethylenediamine, propylenediamine, piperazine, and tris(2-diaminoethyl)amine.
3. A process according to claim 1 wherein the polyfunctional acid halide is selected from the group consisting of trimesoyl chloride, trimellitic acid chloride, isophthaloyl chloride, and terephthaloyl chloride.
4. A process according to claim 1 wherein the porous support membrane comprises nanoparticles.
5. A process according to claim 1 wherein the nanoparticles comprise zeolites.
6. A process according to claim 1 wherein the nanoparticles comprises carbon nanotubes.
7. A process for preparing a reverse osmosis membrane, comprising:
(A) providing a polyamine, a polyfunctional acid halide, and mono-hydrolyzed trimesoyl chloride;
(B) combining the polyamine, polyfunctional acid halide, and mono-hydrolyzed trimesoyl chloride on the surface of a porous support membrane; and
(C) interfacially polymerizing the polyamine and the polyfunctional acyl halide on the surface of the porous support membrane to form a reverse osmosis membrane comprising (i) the porous support membrane and (ii) a discrimination layer comprising a polyamide,
wherein the reverse osmosis membrane is characterized by a flux that is greater than the flux of the same membrane prepared in the absence of the mono-hydrolyzed trimesoyl chloride.
8. A reverse osmosis membrane according to claim 1 or 7 wherein the membrane is capable of exhibiting a flux of at least 30 gfd, determined by exposing the membrane to deionized water containing 32,000 ppm NaCl at a temperature of 25° C. and a pressure of 800 psi.
9. A reverse osmosis membrane according to claim 8 wherein the membrane is capable of exhibiting a salt rejection of at least 99.5%, determined by exposing the membrane to deionized water containing 32,000 ppm NaCl at a temperature of 25° C. and a pressure of 800 psi.
10. A method of purifying brackish water or seawater comprising contacting the brackish water or seawater with a reverse osmosis membrane according to claim 8 .