Particulate water absorbent and process for production thereof
A particulate water absorbing agent of the present invention is a water absorbing agent containing a water absorbing resin as a main component, the particulate water absorbing agent containing a polyvalent metal cation and satisfying: (1) the polyvalent metal cation is contained in an amount between 0.001 wt % and 5 wt % relative to the amount of the water absorbing agent; (2) an absorbency without pressure (CRC) is not less than 28 (g/g) and an absorbency against pressure (AAP 4.83 kPa) is not less than 10 (g/g); (3) the absorbency against pressure and the absorbency without pressure satisfy 77≦AAP (4.83 kPa)+1.8×CRC≦100; and (4) a moisture content of the water absorbing agent is between 5 wt % and 20 wt %. This provides a water absorbing agent which has blocking resistance after moisture absorption, is excellent in stability to shock and suppresses Re-Wet when used in a diaper.
1. A particulate water absorbing agent comprising:
a water absorbing resin as a main component, wherein the water absorbing resin comprises a polyacrylic acid (salt) crosslinked polymer;
a polyvalent metal, wherein the polyvalent metal is a metallic soap and/or a water-soluble polyvalent metal salt; and
a dispersion stabilizer;
wherein said particulate water absorbing agent has:
(1) a polyvalent metal cation in an amount between 0.001 wt % and 5 wt % relative to the amount of the particulate water absorbing agent;
(2) an absorbency without pressure (CRC) of not less than 28 (g/g) and not more than 60 (g/g), and an absorbency against pressure (AAP 4.83 kPa) of not less than 10 (g/g) and not more than 40 (g/g);
(3) the absorbency against pressure and the absorbency without pressure satisfy the inequality: 77≦Absorbency against pressure (AAP 4.83 kPa)+1.8×Absorbency without pressure (CRC)≦100;
(4) a moisture content between 5 wt % and 20 wt %; and
(5) a dusting rate between 0 wt % and 0.8 wt %.
2. The particulate water absorbing agent according to claim 1 , wherein a vertical diffusion absorbency under pressure (VDAUP) is not less than 15 g.
3. The particulate water absorbing agent according to claim 1 , which satisfies any one of the following (A) through (C):
(A) the particulate water absorbing agent is obtained by mixing an aqueous dispersion containing a metallic soap and a dispersion stabilizer with the water absorbing resin;
(B) the particulate water absorbing agent is obtained by a method including the steps of adding a metallic soap and water to the water absorbing resin and controlling a moisture content of the water absorbing agent to between 5 wt % and 20 wt %; and
(C) the particulate water absorbing agent is obtained by carrying out a surface treatment method for water absorbing resin, the method including the steps of (i) mixing an acid radical-containing radical-polymerizable monomer, a polyvalent metal compound and water with the water absorbing resin which is a polyacrylic acid (salt) crosslinked polymer and (ii) polymerizing the acid radical-containing radical-polymerizable monomer.
4. The particulate water absorbing agent according to claim 1 , wherein:
the metallic soap is contained in an amount between 0.001 and 5 parts by weight relative to 100 parts by weight of the water absorbing resin; and
the dispersion stabilizer is contained in an amount between 0.0001 and 1 part by weight relative to 100 parts by weight of the water absorbing resin.
5. The particulate water absorbing agent according to claim 1 , wherein the dispersion stabilizer is a surfactant.
6. The particulate water absorbing agent according to claim 1 , wherein the water absorbing resin is a surface-crosslinked water absorbing resin.
7. The particulate water absorbing agent according to claim 1 , wherein a blocking rate after moisture absorption is between 0 wt % and 10 wt %.
8. The particulate water absorbing agent according to claim 1 , which is obtained by granulating water absorbing resin particles.
9. An absorbing article comprising a particulate water absorbing agent recited in claim 1 .
10. The particulate water absorbing agent according to claim 1 , wherein:
the absorbency against pressure and the absorbency without pressure satisfy the inequality: 77≦Absorbency against pressure (AAP 4.83 kPa)+1.8×Absorbency without pressure (CRC)≦90.