Method for the spot repair of scratch-resistant paint films
A spot repair method of scratch-resistant paint film: (a) sanding a part to be repaired having a scratch-resistant clear paint film thereon, (b) sanding a part to be clear gradation painted outside the part to be repaired with an abrasive material, (c) painting the part to be repaired with a color base-paint, (d) applying a clear paint wet-on-wet without curing the color base-paint, (e) applying a clear paint diluted with a gradation agent to the part to be gradation painted, (f) drying the applied paints, and (g) polishing the dried parts, wherein (1) the clear paint is a two-liquid type having an isocyanate curing agent and (2) the gradation agent comprises from 5 to 50 mass % ethyl ethoxypropionate, from 1 to 5 mass % of an acrylic resin as solid fraction, a surfactant and a curing catalyst.
1. A method for the spot repair of a scratch-resistant paint film comprising:
(a) sanding a part which is the subject of a repair with a sanding material, the part to be repaired having a scratch-resistant clear paint film thereon,
(b) sanding a part which is to be clear gradation painted outside the part to be repaired with an abrasive material,
(c) painting the part to be repaired with a color base-paint,
(d) applying a clear paint wet-on-wet to the part to be repaired without curing the color base-paint,
(e) applying a clear paint which has been diluted with a gradation agent to the part which is to be clear gradation painted,
(f) drying the painted parts, and
(g) polishing the parts which have been gradation painted,
wherein
(1) the clear paint is a two-liquid paint comprising an isocyanate curing agent; and
(2) the gradation agent comprises:
a solvent which comprises ethyl ethoxypropionate, wherein the amount of the solvent in the gradation agent is from 90 to 98 mass % and the amount of ethyl ethoxypropionate in the gradation agent is from 5 to 50 mass %;
an acrylic resin, wherein the amount of the acrylic resin in the gradation agent as solid fraction is from 1 to 5 mass %;
a surfactant, wherein the amount of the surfactant in the gradation agent is from 0.05 to 1 mass %; and
a curing catalyst which is a metal catalyst, wherein the amount of the catalyst in the gradation agent is from 0.1 to 2 mass %;
wherein the acrylic resin is a copolymer of a hydroxyl group-containing ethylenically unsaturated monomer and one or more alkyl ester-based ethylenically unsaturated monomers, wherein the hydroxyl group-containing ethylenically unsaturated monomer comprises hydroxyethyl (meth)acrylate or hydroxypropyl (meth)acrylate, and the alky ester-based ethylenically unsaturated monomer comprises at least one of: 2-ethylhexyl (meth)acrylate, n-decyl (meth)acrylate, and isodecyl (meth)acrylate; and wherein the acrylic resin has an OH-group value of 50 to 200 mg KOH/g and a weight-average molecular weight of 1,000 to 30,000.
2. The method of claim 1 further comprising (d′) applying a clear paint which has been diluted with a diluting solvent between process (d) and process (e).
3. The method of claim 1 , wherein the abrasive material is finer than the sanding material.
4. The method claim 1 , wherein in (e) a mixing proportion as a ratio by mass in the range of 100/100 to 1/100 of the clear paint to the gradation agent.
5. The method of claim 1 , wherein the solvent further comprises butyl acetate.