Method of preparing ZSM-5 zeolite using nanocrystalline ZSM-5 seeds
A method of preparing ZSM-5, including: providing a nanocrystalline ZSM-5 seed having a size of 70-150 nm; adding the nanocrystalline ZSM-5 seed to a stock solution including water glass as a silica source, an alumina source, a neutralizer and water to form a reaction mixture; and maintaining the reaction mixture at 150-200° C. to crystallize the reaction mixture. The method is advantageous in that ZSM-5 having small and uniform crystal sizes and including no impurities can be synthesized in a short period of time.
1. A method of preparing ZSM-5, comprising:
providing a nanocrystalline ZSM-5 seed having a size of about 70 about 150 nm from organic structure-inducing material, a silica source and an alumina source,
adding the nanocrystalline ZSM-5 seed to a stock solution including water glass as a silica source, an alumina source, a neutralizer and water to form a reaction mixture, wherein the solution has a composition represented by [Na 2 O] X [Al 2 O 3 ] Y [SiO 2 ] 100 [H 2 O] Z in which X is about 10 to about 26 (mole), Y is about 0.2 to about 5 (mole), and Z is about 2500 to about 4000 (mole); and
maintaining the reaction mixture at about 150 to about 200° C. to crystallize the reaction mixture.
2. The method of preparing ZSM-5 according to claim 1 , wherein the nanocrystalline ZSM-5 seed is included in an amount of about 0.1 to about 6 wt % based on the reaction mixture.
3. The method of preparing ZSM-5 according to claim 1 , wherein the alumina source is one or more selected from sodium aluminate, aluminum nitrate, aluminum chloride, aluminum acetate, aluminum sulfate, aluminum isopropoxide, and aluminum acetylacetonate.
4. The method of preparing ZSM-5 according to claim 1 , wherein the neutralizer is any one selected from hydrochloric acid, nitric acid, phosphoric acid, sulfuric acid, and aluminum sulfate.
5. The method of preparing ZSM-5 according to claim 1 , wherein the crystallizing of the reaction mixture is performed for 12˜72 hours.