Process of making a carbon fiber nonwoven fabric
View Patent ↗The present invention has an object of providing the carbon fiber (or the nonwoven fabric configured of the aforementioned carbon fiber) of which the surface area, the graphitization degree, and the fiber diameter are large, high, and small, respectively, and yet of which dispersion is small. The method of producing the carbon fiber nonwoven fabric includes a dispersion liquid preparing step of preparing a dispersion liquid containing resin and pitch, an electrospinning step of producing the nonwoven fabric that is comprised of carbon fiber precursors with electrospinning from the aforementioned dispersion liquid, and a modifying step of modifying the carbon fiber precursors of the nonwoven fabric obtained in the aforementioned electrospinning step into the carbon fiber.
1. A method of producing a carbon fiber nonwoven fabric, the method comprising:
preparing a dispersion liquid comprising a resin and a pitch;
electrospinning from the dispersion liquid to obtain a nonwoven fabric comprising carbon fiber precursors; and
modifying the carbon fiber precursors of the nonwoven fabric into carbon fiber, to obtain a carbon fiber nonwoven fabric,
wherein the carbon fiber comprises a large diameter portion and a small diameter portion.
2. The method of claim 1 , wherein the modifying comprises heating the nonwoven fabric to 50 to 4000° C.
3. The method of claim 1 , wherein the modifying comprises removing the resin from the nonwoven fabric.
4. The method of claim 3 , wherein the removing comprises heating the nonwoven fabric under an oxidizing gas atmosphere.
5. The method of claim 1 , wherein the modifying comprises performing a carbonizing process for the nonwoven fabric.
6. The method of claim 5 , wherein the modifying comprises performing a graphitizing process for the nonwoven fabric.
7. The method claim 6 , wherein the graphitizing process comprises heating the nonwoven fabric under an inert atmosphere.
8. The method of claim 1 , wherein the resin is water-soluble.
9. The method of claim 1 , wherein the resin is pyrolytic.
10. The method of claim 1 , wherein the resin is a polyvinyl alcohol.
11. The method of claim 1 , wherein the pitch is a mesophase pitch.
12. The method of claim 1 , wherein the pitch has a particle diameter of 1 nm to 10 μm.
13. The method of claim 1 , wherein the pitch has a particle diameter of 100 nm to 1 μm.
14. The method of claim 1 , wherein the dispersion liquid comprises 20 to 200 parts by mass per 100 parts by mass of the resin.
15. The method of claim 1 , wherein the dispersion liquid further comprises at least one solvent.
16. The method of claim 15 , wherein the solvent is water.
17. The method of claim 15 , wherein the solvent comprises at least one member selected from the group consisting of water, acetic acid, formic acid, methanol, ethanol, propanol, butanol, isobutyl alcohol, amyl alcohol, isoamyl alcohol, cyclohexanol, ethyl acetate, butyl acetate, diethyl ether, dibutyl ether, tetrahydrofuran, acetone, methyl ethyl ketone, methyl isobutyl ketone, N,N′-dimetyl formamide, dimetyl sulfoxide, acetonitrile, dimethyl acetamide, chloroform, tetrachloromethane and hexafluoroisopropyl alcohol.
18. The method of claim 15 , wherein the solvent is comprises at least one alcohol.
19. The method of claim 1 , wherein the carbon fiber comprises a large diameter portion having a diameter of 20 nm to 2 μm and a small diameter portion having a diameter of 10 nm to 1 μm.
20. The method of claim 1 , wherein the carbon fiber comprises a large diameter portion having a diameter of 50 nm to 1 μm and a small diameter portion having a diameter of 20 nm to 500 nm.
21. The method of claim 1 , wherein the (a maximum value of the diameter in the aforementioned large diameter portion)/(a minimum value of the diameter in the aforementioned small diameter portion)=1.1 to 100.
22. The method of claim 1 , wherein the (a maximum value of the diameter in the aforementioned large diameter portion)/(a minimum value of the diameter in the aforementioned small diameter portion)=2 to 50.
23. The method of claim 1 , wherein the full length of the carbon fiber is 0.1 to 1000 μm.
24. The method of claim 1 , wherein the large diameter portion has a diameter of 20 nm to 5 μm and the small diameter portion has a diameter of 10 nm to 3 μm.
25. The method of claim 1 , wherein the large diameter portion has a diameter of 20 nm to 5 μm and the small diameter portion has a diameter of 10 nm to 3 μm, and wherein the average diameter of the large diameter portion is greater than the average diameter of the small diameter portion.