Compositions comprising polylactic acid, bentonite, and gum arabic
Biodegradable materials and, in particular, compositions comprising polylactic acid, bentonite, and gum arabic are provided. Processes, methods and uses involving polylactic acid are further provided.
1. An extrusion method of producing an extruded plastic, the extrusion method comprising:
(a) providing a composition having a moisture content of about 1% by weight or less, comprising polylactic acid, bentonite, and gum Arabic;
(b) thermally compounding the composition through an extruder, the extruder extending through a plurality of temperature zones comprising three temperature zones: a first temperature zone at 350 ° F., a second temperature zone at 320 ° F., and a third temperature zone at 310 ° F.; each temperature zone being above the melt temperature of the composition; and
(c) extruding the composition through the extruder, thereby producing the extruded plastic.
2. A method according to claim 1 wherein the composition comprises from about 1% to 20% by weight bentonite.
3. A method according to claim 1 wherein the composition comprises from about 0.01% to about 25% by weight gum Arabic.
4. A method according to claim 1 wherein the composition is ASTM D-6400 compliant.
5. A method according to claim 1 wherein the composition disintegrates by about 50% or more within 28 days under the conditions specified in ASTM D-5526.
6. A method of producing an injection molded article, said method comprising:
(a) producing an extruded plastic by the method of claim 1 , wherein the extruded plastic comprises a composition having a moisture content of about 1% by weight or less, comprising polyactic acid, bentonite, and gum Arabic;
(b) pelletizing the extruded plastic to provide pellets;
(c) extruding the pellets through a screw extruder having a plurality of temperature zones to provide a molten composition;
(d) injecting the molten composition under pressure into a mold; and
(e) cooling the molten composition to below its melt temperature, thereby producing the injection molded article.
7. A method according to claim 6 wherein the composition comprises from about 1% to 20% by weight bentonite.
8. A method according to claim 6 wherein the composition comprises from about 0.01% to about 25% by weight gum Arabic.
9. A method according to claim 6 wherein the composition is ASTM D-6400 compliant.
10. A method according to claim 6 wherein the composition disintegrates by about 50% or more within 28 days under the conditions specified in ASTM D-5526.