Method of producing polarizing film
The present invention provides a method of producing a polarizing film having excellent optical characteristics. The method of producing a polarizing film of the present invention includes: forming a polyvinyl alcohol-based resin layer 12 on a thermoplastic resin substrate 11 to produce a laminate 10 ; dyeing the polyvinyl alcohol-based resin layer 12 of the laminate 10 with iodine; stretching the laminate 10 ; and covering, after the dyeing and the stretching, a surface of the polyvinyl alcohol-based resin layer 12 of the laminate 10 with a cover film having a moisture permeability of 100 g/m 2 ·24 h or less, followed by heating of the laminate 10 under the state.
1. A method of producing a polarizing film, comprising:
forming a polyvinyl alcohol-based resin layer on a thermoplastic resin substrate to produce a laminate;
dyeing the polyvinyl alcohol-based resin layer of the laminate with iodine;
stretching the laminate; and
covering, after the dyeing and the stretching, a surface of the polyvinyl alcohol-based resin layer of the laminate with a cover film having a moisture permeability of 100 g/m 2 ·24 h or less, followed by heating of the laminate.
2. A method of producing a polarizing film according to claim 1 , wherein the heating is performed at a temperature of 60° C. or more.
3. A method of producing a polarizing film according to claim 1 , wherein the surface of the polyvinyl alcohol-based resin layer is covered with the cover film through an adhesive.
4. A method of producing a polarizing film according to claim 3 , wherein the adhesive comprises an aqueous adhesive.
5. A method of producing a polarizing film according to claim 1 , wherein the thermoplastic resin substrate after the stretching has a moisture permeability of 100 g/m 2 ·24 h or less.
6. A method of producing a polarizing film according to claim 1 , wherein the stretching includes underwater stretching in an aqueous solution of boric acid.
7. A method of producing a polarizing film according to claim 6 , comprising subjecting the laminate to aerial stretching at 95° C. or more before the dyeing and the boric acid underwater stretching.
8. A method of producing a polarizing film according to claim 1 , wherein a stretching ratio of the laminate is 5.0 times or more.
9. A method of producing a polarizing film according to claim 1 , wherein the thermoplastic resin substrate is constituted of an amorphous polyethylene terephthalate-based resin.