Anisotropy reduction in coating of conductive films
View Patent ↗Provided herein is a method of forming a conductive film, the method comprising: providing a coating solution having a plurality of conductive nanostructures and a fluid carrier; moving a web in a machine direction; forming a wet film by depositing the coating solution on the moving web, wherein the wet film has a first dimension extending parallel to the machine direction and a second dimension transverse to the machine direction; applying an air flow across the wet film along the second dimension, whereby at least some of the conductive nanostructures in the wet film are reoriented; and allowing the wet film to dry to provide the conductive film.
1. A method of forming a conductive film, comprising:
forming a wet film having a plurality of conductive nanostructures and a fluid carrier, wherein the wet film has a first dimension and a second dimension substantially perpendicular to the first dimension;
applying an air flow and directing the air flow onto the wet film in a direction along the second dimension to reorient a direction of at least some of the plurality of conductive nanostructures in the wet film to define a plurality of reoriented conductive nanostructures; and
drying the wet film having the plurality of reoriented conductive nanostructures to provide the conductive film.
2. The method of claim 1 , wherein the wet film is formed by slot die coating.
3. The method of claim 1 , wherein forming the wet film comprises:
providing a coating solution having the plurality of conductive nanostructures and the fluid carrier on a web; and
moving the web in a direction along the first dimension.
4. The method of claim 3 , wherein the plurality of conductive nanostructures are made of a plurality of silver nanowires.
5. The method of claim 3 , wherein the fluid carrier at least comprises a viscosity modifier and water.
6. The method of claim 3 , wherein the wet film is continuously formed on the web as the web moves in the direction along the first dimension.
7. The method of claim 6 , wherein the air flow is continuously applied as the wet film is continuously formed.
8. The method of claim 3 , wherein the air flow is applied within 30 seconds following providing the coating solution.
9. The method of claim 1 , wherein the air flow originates from a lateral side of the wet film.
10. The method of claim 1 , wherein the air flow originates from a top side of the wet film.