Method of making a hydrogen transport membrane, and article
The present invention relates to a method of manufacturing a hydrogen transport membrane and the composite article itself. More specifically, the invention relates to producing a membrane substrate, wherein the ceramic substrate is coated with a metal oxide slurry, thereby eliminating the need for an activation step prior to plating the ceramic membrane through an electroless plating process. The invention also relates to modifying the pore size and porosity of the substrate by oxidation or reduction of the particles deposited by the metal oxide slurry.
1. A method of forming a membrane substrate, wherein the method comprises:
forming a porous ceramic substrate, treating one surface of said ceramic substrate with a metal based slurry, wherein the metal is selected from the group consisting of nickel, iron, gold, copper, platinum, palladium, silver, manganese, chromium, ruthenium, zinc and oxides thereof to deposit metal or metal oxide particles on said substrate wherein the surface pore size is reduced by oxidation or reduction; and
depositing a dense layer of palladium or palladium alloy by electroless plating directly to a surface treated with the metal oxide, wherein the pore size of the treated surface has been reduced, thereby forming a membrane permeable to hydrogen.
2. The method of claim 1 , wherein the substrate is employed as a component of a composite gas separation membrane.
3. The method of claim 1 , further comprising depositing a layer of palladium or palladium alloy onto said porous ceramic substrate forming a composite hydrogen transport membrane for separating hydrogen from a hydrogen containing feed.
4. The method of claim 1 , wherein the composition of the solids in the slurry is about 60-70 wt % yttria-stabilized zirconia with about 20-30 wt % nickel oxide, and a balance of carbon black.
5. The method of claim 1 , wherein the porous ceramic substrate is extruded into tubes.
6. The method of claim 1 , wherein the method of forming the composite hydrogen transport membrane is by electroless plating in the absence of an activation step.
7. The method of claim 1 , wherein the ceramic substrate is prepared by (a) mixing yttria stabilized zirconia with carbon black to form a blend; (b) adding the blend to a mixer at a controlled temperature to form a paste; (c) extruding the paste into tubes; (d) treating the tubes with a metal oxide based slurry; (e) sintering the treated tubes; and (f) depositing a palladium or palladium alloy onto the tubes by an electroless plating process.
8. The method of claim 1 , wherein the pore size and porosity of the ceramic substrate are modified by oxidation or reduction of the metal or metal oxide.
9. A composite hydrogen transport membrane, comprising:
a porous ceramic substrate having two surfaces, wherein at least one surface of said substrate has been treated with a metal oxide slurry, wherein the metal is selected from the group consisting of nickel, iron, gold, copper, platinum, palladium, silver, manganese, chromium, ruthenium, zinc and oxides thereof forming active sites wherein the pore size of the surface to be plated is modified by oxidation or reduction before depositing a palladium metal or palladium alloy layer directly to one of the surfaces of said ceramic substrate via an electroless plating process, where said palladium metal or palladium alloy has plated to a surface treated with the metal oxide, wherein the pore size of the treated surface has been reduced, thereby funning a membrane permeable to hydrogen.
10. The composite hydrogen transport membrane of claim 9 , wherein the composition of solids in the metal oxide slurry employed in treating the porous ceramic substrate is about 60-70 wt % yttria stabilized zirconia with about 20-30 wt % nickel oxide and a balance of carbon black.
11. A method of forming a composite transport membrane to separate component from a component containing feed gas, wherein the method comprises:
forming a porous ceramic substrate, treating said ceramic substrate with a metal or metal oxide based slurry to deposit a metal selected from the group consisting of nickel, iron, gold, copper, platinum, palladium, silver, manganese, chromium, ruthenium, zinc and oxides thereof on said substrate in order to develop an affinity for the metal deposited, where the pore size at a surface of said ceramic substrate is reduced by oxidation or reduction, and
depositing a dense layer of palladium or palladium alloy by electroless plating onto said ceramic substrate to form a composite hydrogen transport membrane for separating said component from said component containing feed gas.