Antireflection coating film and antireflection coating material for optical element and optical element
An antireflection coating film for an optical element is provided on a surface of a substrate of an optical material and includes first particles having a refractive index (nd) of at least 2.2 or more for the d-line and an average particle size of 10 to 70 nm, second particles of at least one of silica and sericite and having an average particle size of 1 to 11 μm, a colorant of an organic substance and soluble in an organic solvent, and a resin, in which the first particle content is in the range of 10% to 35% by weight, and second particle content is in the range of 1% to 11% by weight. The antireflection coating film has a high effect of preventing surface reflection, a high effect of preventing inner-surface reflection, satisfactory absorption of visible light, and low levels of reflection and scattering in the film.
1. A light-shielding coating film for an optical element, the film being formed on a surface of a substrate composed of an optical material, the light-shielding coating film comprising:
first particles at least having a refractive index (nd) of 2.2 to 3.5 for the d-line and an average particle size of 10 nm to 70 nm;
second particles composed of at least one of silica and sericite, the second particles having an average particle size of 1 μm to 11 μm;
a colorant; and
a resin,
wherein the first particle content is in the range of 10% by weight to 35% by weight, and second particle content is in the range of 1% by weight to 11% by weight, and
wherein the ratio of the minimum absorbance to the maximum absorbance (minimum absorbance/maximum absorbance) of the light-shielding coating film for the optical element in the wavelength range of 400 nm to 700 nm is 0.7 or more.
2. The light-shielding coating film for an optical element according to claim 1 ,
wherein the percentage by number of particles having a particle size of 100 nm or more in the first particles is 0.3% or less.
3. The light-shielding coating film for an optical element according to claim 1 ,
wherein the first particles contain at least one of titania and zirconia.
4. The light-shielding coating film for an optical element according to claim 1 ,
wherein the colorant composed of an organic substance and soluble in an organic solvent is a dye.
5. A light-shielding coating material for an optical element, comprising:
an organic solvent;
first particles having a refractive index (nd) of 2.2 to 3.5 for the d-line and an average particle size of 10 nm to 70 nm;
second particles composed of at least one of silica and sericite, the second particles having an average particle size of 1 μm to 11 μm;
a colorant composed of an organic solvent; and
a resin,
wherein with respect to the solid content excluding the organic solvent, the first particle content is in the range of 10% by weight to 35% by weight, and second particle content is in the range of 1% by weight to 11% by weight, and
wherein the ration of the minimum absorbance to the maximum absorbance (minimum absorbance/maximum absorbance) of the light-shielding coating material for the optical element in the wavelength range of 400 nm to 700 nm is 0.7 or more.
6. An optical element comprising:
a substrate composed of an optical material; and
a light-shielding coating film provided on a portion of a circumferential surface of the substrate,
the light-shielding coating film comprising:
first particles having a refractive index (nd) of 2.2 to 3.5 for the d-line and an average particle size of 10 nm to 70 nm;
second particles composed of at least one of silica and sericite, the second particles having an average particle size of 1 μm to 11 μm;
a coloran; and
a resin,
wherein the first particle content is in the range of 10% by weight to 35%by weight, and second particle content is in the range of 1% by weight to 11% by weight, and
wherein the ratio of the minimum absorbance to the maximum absorbance (minimum absorbance/maximum absorbance) of the light-shielding coating film for the optical element in the wavelength range of 400 nm to 700 is 0.7 or more.