Thick film silver paste and its use in the manufacture of semiconductor devices
View Patent ↗The present invention is directed to an electroconductive silver thick film paste composition comprising Ag, a glass frit and rhodium resinate, Cr 2 O 3 or a mixture thereof all dispersed in an organic medium. The present invention is further directed to an electrode formed from the paste composition and a semiconductor device and, in particular, a solar cell comprising such an electrode. The paste is particularly useful for forming a tabbing electrode.
1. A thick film paste composition comprising:
(a) 35-55 wt % Ag;
(b) 0.5-6 wt % glass frit, wherein said glass frit is a Pb-free bismuth-tellurium-oxide consisting of 22-42 wt % Bi 2 O 3, 58-78 wt % TeO 2, 0.1-7 wt % Li 2 O and 0.1-4 wt % TiO 2 , based on the total weight of said bismuth-tellurium-oxide;
(c) 0.08-0.4 wt % of a component selected from the group consisting of rhodium resinate, Cr 2 O 3 and mixtures thereof; and
(d) organic medium;
wherein said Ag, said glass frit and said component selected from the group consisting of rhodium resinate, Cr 2 O 3 and mixtures thereof are dispersed in said organic medium and wherein the wt % of said Ag, said glass frit and said component selected from the group consisting of rhodium resinate, Cr 2 O 3 and mixtures thereof are based on the total weight of said paste composition.
2. A solar cell comprising an electrode formed from the paste composition of claim 1 , wherein said paste composition has been deposited on the back side of said solar cell and has been fired to remove the organic medium and form a tabbing electrode on the back side of said solar cell.