Polyolefin microporous membrane and method of producing the same, separator for non-aqueous secondary battery and non-aqueous secondary battery
The present invention provides a polyolefin microporous membrane in which a degree of crystallinity is from 60 to 85%, and a tie molecular volume fraction is from 0.7 to 1.7%.
1. A method of producing a polyolefin microporous membrane, wherein a degree of crystallinity is from 60 to 85%, and a tie molecule volume fraction is from 0.7 to 1.7%, the method comprising:
preparing a polyolefin solution by kneading from 1 to 35 parts by mass of polyolefin and from 65 to 99 parts by mass of mixed solvent composed of a volatile solvent and a nonvolatile solvent at from 190 to 220° C.;
forming a gel composition by extruding the polyolefin solution through a die at a temperature from the melting point of the polyolefin to the melting point +60° C. and cooling the extruded polyolefin solution;
removing the volatile solvent from the gel composition;
drawing the gel composition; and
removing the nonvolatile solvent from the gel composition.
2. The method of producing the polyolefin microporous membrane according to claim 1 , wherein the tie molecule volume fraction of the polyolefin is from 0.7 to 1.5%.
3. The method of producing the polyolefin microporous membrane according to claim 1 , wherein a number average molecular weight is from 30,000 to 80,000.
4. The method of producing the polyolefin microporous membrane according to claim 1 , wherein a number of short chain branches contained in 1000 carbon atoms in a main chain of the polyolefin is from 1 to 5.
5. The method of producing the polyolefin microporous membrane according to claim 1 , comprising a polyolefin containing an ultra-high molecular weight polyethylene having a weight-average molecular weight of 1,000,000 or higher and a high-density polyethylene having a density of 0.942 g/cm 3 .