Metal fluoride compositions for self formed batteries
The described invention provides compositions related to an electronically insulating amorphous or nanocrystalline mixed ionic conductor composition comprising a metal fluoride composite to which an electrical potential is applied to form 1) a negative electrode, and 2) a positive electrode, wherein the negative electrode and positive electrode are formed in situ.
1. A precursor for a self-formed battery, comprising
an amorphous or nanocrystalline mixed ionic conductor composition, including an alkali metal fluoride and a fluoride glass former composite;
a positive reactive current collector in contact with the composition; and
a negative reactive current collector in contact with the composition;
wherein the alkali metal fluoride: metal fluoride glass former molar ratio is in the range from 15:1 to 1:1, and wherein the composition is electronically insulating and forms in situ a negative electrode and a positive electrode when an electrical potential is applied thereto.
2. The precursor according to claim 1 , wherein the composition conducts cations and anions as charge carriers.
3. The precursor according to claim 2 , wherein the anions are fluoride anions.
4. The precursor according to claim 2 , wherein the cations are cations of an alkali metal.
5. The precursor according to claim 4 , wherein the alkali metal cations are lithium cations.
6. The precursor according to any one of claims 1 , 2 and 3 , wherein the alkali metal fluoride: metal fluoride glass former molar ratio is in the range from 10:1 to 2:1.
7. The precursor according to claim 6 , wherein the alkali metal fluoride: metal fluoride glass former molar ratio is in the range from 9:1 to 2:1.
8. The precursor according to claim 1 , wherein the fluoride glass former is selected from the group consisting of AlF 3 , ZrF 4 , GaF 3 , HfF 4 , YbF 3 , ThF 3 , ZnF 2 InF 3 , UF 3 , YF 3 , and combinations thereof.
9. The precursor according to any one of claims 1 , 2 , and 3 , wherein the composition further comprises a fluoride glass network modifier.
10. The precursor according to claim 9 , wherein the akali metal fluoride: glass network modifier molar ratio is in the range from 20:1 to 1:1.
11. The precursor according to claim 10 , wherein the glass network modifier is selected from the group consisting of LaF ' , BiF 3 , PbF 2 , KF, CaF 2 , BaF 2 , SnF 2 , SrF, 2 , or a rare earth metal fluoride.
12. The precursor according to claim 9 , wherein the glass network modifier is selected from the group consisting of LaF 3 , BiF 3 , PbF 2 , KF, CaF 2 , BaF 2 , SnF 2 , SrF 2 . or a rare earth metal fluoride.
13. The precursor according to claim 1 , wherein the alkali metal fluoride is LiF.
14. The precursor according to claim 1 , wherein the positive reactive current collector comprises at least one of Ag, Au, Bi, Pb, Sn, Cu, Pt, Pd, Fe, Mn, Ni, Mo, V or a combination thereof.
15. The precursor according to claim 14 , wherein the positive reactive current collector further comprises at least one of La, Ca, Ba, Sr, O, and S.
16. The precursor according to claim 1 , wherein the positive reactive current collector comprises carbon.
17. The precursor according to claim 16 , wherein the carbon is in the form of one or both of a carbon nanotube or graphene.
18. The, precursor according to claim 1 , wherein the negative reactive current collector comprises at least one of Ag, In, Al, Si, Sn, Ge, Mg, Au, Pd, Bi, Pb, graphite, carbon nanotubes, graphene, or a combination thereof.
19. The precursor according to claim 1 , wherein the positive reactive current collector is a compositionally graded material that allows part of the positive reactive current collector to electrochemically oxidize to form the positive electrode or to electrochemically reduce to form the negative electrode.
20. The precursor according to claim 1 wherein the alkali metal fluoride: metal fluoride glass former molar ratio is in the range from 15:1 to 2:1.
21. The precursor according to claim 1 , wherein the negative reactive current collector is a compositionally graded material that allows part of the negative reactive current collector to electrochemically oxidize to form the positive electrode or to electrochemically reduce to form the negative electrode.
22. A precursor d battery, comprising
an amorphous or nanocrystalline mixed ionic conductor composition, including an alkali metal fluoride and a fluoride glass former composite;
a positive reactive current collector; and,
a negative reactive current collector,
wherein one of the positive reactive current collector and the negative current collector is in contact with the composition and the other of the positive current collector and the negative current collector is not in contact with the composition, and the alkali metal fluoride: metal fluoride glass former molar ratio is in the range from 15:1 to 1:1, and wherein the composition is electronically insulating and forms in situ a negative electrode and a positive electrode when an electrical potential is applied thereto.
23. The precursor according to claim 22 , wherein the one of the positive reactive current collector and the negative current collector that is in contact with the position has a coating that includes the composition, the material further comprising a nonaqueous liquid electrolyte between the other of the positive current collector and the negative current collector and the coating.