Polycrystalline AL
View Patent ↗The present invention relates to polycrystalline Al 2 O 3 bodies based on melted aluminum oxide having a mean crystallite size of the primary crystals between 20 μm and 100 μm and a closed macroporosity between 10% by volume and 30% by volume. The polycrystalline Al 2 O 3 bodies may be obtained by tapping out and quenching a liquid aluminum oxide melt and simultaneous seeding of the pouring stream with seed crystals and can be used advantageously for the production of abrasive materials and refractory products.
1. Polycrystalline Al 2 O 3 bodies based on melted aluminum oxide having a content of α-aluminum oxide of greater than 98% by weight, made up of a plurality of Al 2 O 3 primary crystals having a crystallite size between 20 μm and 100 μm characterized in that the Al 2 O 3 bodies have a closed macroporosity having a pore volume between 10% by volume and 30% by volume, wherein the mean diameter of the pores is between 10 μm and 100 μm and the maximum pore diameter is about 120 μm.
2. The Al 2 O 3 bodies according to claim 1 , characterized in that the primary crystals have a size ranging between 30 μm and 60 μm.
3. The Al 2 O 3 bodies according to claim 1 , characterized in that the content of α-aluminum oxide is greater than 99.5% by weight.
4. The Al 2 O 3 bodies according to claim 2 , characterized in that the content of α-aluminum oxide is greater than 99.5% by weight.
5. The Al 2 O 3 bodies according to claim 1 , characterized in that the primary crystals have a pseudo-cubic crystal shape.
6. The Al 2 O 3 bodies according to claim 2 , characterized in that the primary crystals have a pseudo-cubic crystal shape.
7. The Al 2 O 3 bodies according to claim 3 , characterized in that the primary crystals have a pseudo-cubic crystal shape.
8. A process for the production of polycrystalline Al 2 O 3 bodies according to claim 1 based on electrically melted aluminum oxide, the process comprising:
melting aluminum oxide in an electric-arc furnace;
tapping out the liquid aluminum oxide melt at a constant rate of less than 80 kg/min;
seeding the pouring stream of the liquid melt with seed crystals of α- and/or γ-aluminum oxide having a mean particle diameter d 50 of 50 μm to 90 μm;
cooling of the liquid melt in order to obtain a solid aluminum oxide body; and
fragmentizing the solid aluminum oxide body in order to obtain the polycrystalline Al 2 O 3 bodies.
9. The process according to claim 8 , characterized in that the melt is tapped out at a constant pour rate of less than 40 kg/min.
10. The process according to claim 8 , characterized in that the seeding of the pouring stream occurs by directly blowing the aluminum-oxide seed crystals into the pouring stream.
11. The process according to claim 9 , characterized in that the seeding of the pouring stream occurs by directly blowing the aluminum-oxide seed crystals into the pouring stream.
12. The process according to claim 9 , characterized in that the quantity of seed crystals is between 5% and 20% by weight, based on the quantity of melted aluminum oxide.
13. The process according to claim 8 , characterized in that cooling of the melt is effected by means of water-cooled rollers, by pouring the melt between cooling plates made of metal, or by pouring the melt onto cooling plates.
14. Use of the polycrystalline Al 2 O 3 bodies according to claim 1 for the production of abrasive and/or fireproof materials.