Heat-protection material
A heat protection material for a surface, made of a mixture comprising a resin, cork granules and refractory fibers; the proportion of cork granules in the mixture is 50 to 80% by mass, wherein the corresponding proportion of refractory fibers in the mixture is 1 to 11% by mass.
1. A heat protection ablative material for protecting a surface of a space vehicle from heat, having a mixture comprising a phenolic resin with a content of coke above 50% when heated to 1,000° C. in an inert atmosphere such as nitrogen, cork granules and refractory fibers, in which the proportion of cork granules in the mixture is a percentage from 70 to 73% by mass, wherein the percentage by mass in the mixture of refractory fibers is between 1 and 3% while the percentage by mass in the mixture of resin is the range of 23-25% and the material being so designed to withstand heat flows ranging from 0.5 to 10 MW/m2, and the material contains no microspheres.
2. Heat protection material according to claim 1 , comprising 0.5 to 1.5% percentage by mass of fungicide.
3. Heat protection material according to claim 1 , wherein the cork is flame-proofed cork.
4. Heat protection material according to claim 1 , comprising a density between 0.35 and 0.41 kg/L after degassing.
5. Heat protection material according to claim 1 , comprising a density of 0.38 kg/L after degassing.
6. Heat protection material according to claim 1 , wherein the refractory fibers are carbon fibers between 0.4 and 4 mm long.
7. Heat protection material according to claim 1 , wherein the refractory fibers are alumina fibers between 0.4 and 4 mm long.
8. A heat protection ablative material for protecting a surface of a space vehicle from heat, having a mixture comprising a phenolic resin with a content of coke above 50% when heated to 1,000° C. in an inert atmosphere such as nitrogen, cork granules and refractory fibers, in which the proportion of cork granules in the mixture is a percentage from 65 to 68% by mass, wherein the percentage by mass in the mixture of refractory fibers is between is between 9 and 11% while the percentage by mass in the mixture of resin is the range of 21-24% the material being so designed to withstand heat flows ranging from 0.5 to 10 MW/m2, the material containing no microspheres.
9. Heat protection material according to claim 8 , comprising 0.5 to 1.5% percentage by mass of fungicide.
10. Heat protection material according to claim 8 , wherein the cork is flame-proofed cork.
11. Heat protection material according to claim 8 , comprising a density between 0.35 and 0.41 kg/L after degassing.
12. Heat protection material according to any claim 8 , comprising a density of 0.38 kg/L after degassing.
13. Heat protection material according to claim 8 , wherein the refractory fibers are carbon fibers between 0.4 and 4 mm long.
14. Heat protection material according to claim 8 , wherein the refractory fibers are alumina fibers between 0.4 and 4 mm long.