Use of organogelator derivatives in bituminous compositions to improve the resistance of same to chemical stress

1. A method for improving resistance to aggressive chemical agents of a bituminous composition, the method comprising adding at least one organogelator derivative to the bituminous composition and contacting the bituminous composition containing the organogelator with petroleum hydrocarbons, the at least one organogelator derivative having a molar mass of less than or equal to 2,000 g·mol −1 and comprising at least one donor of hydrogen bonds D, at least one acceptor of hydrogen bonds A and at least one compatibilizer C in the bitumen, the compatibilizer C comprising a group selected from the group consisting of:

at least one linear hydrocarbon chain comprising at least 4 carbon atoms,

at least one aliphatic cycle with 3 to 8 atoms,

at least one aromatic cycle, and

at least one aliphatic or partly aromatic or further entirely aromatic fused polycyclic system, each cycle comprising 5 or 6 atoms, taken alone or as a mixture, excluding N,N′-ethylene bis(stearamide) and excluding fatty chain polyamines obtained by reacting polyalkylene polyamines with fatty chains of general formula R—NH—(CH 2 —CH 2 —CH 2 —NH) n —H wherein R represents a saturated and/or unsaturated linear hydrocarbon chain, with 8 to 22 carbon atoms, n being an integer from 1 to 5, with formic acid,

and said organogelator derivative is selected from the group consisting of:

a compound of general formula (I): R 1 —CONH—NHCO—R 2 , wherein R 1 and/or R 2 represent the compatibilizer C and represent independently of each other at least one linear hydrocarbon chain comprising at least 4 carbon atoms, or at least one aromatic cycle,

a compound of general formula (II): (R 3 —NHCO) x —Z—(NHCO—R 4 ) y , wherein

R 3 and/or R 4 represent independently of each other, a linear, branched or cyclic, saturated or unsaturated hydrocarbon chain comprising from 1 to 22 carbon atoms;

Z represents the compatibilizer C,

x and y are different integers with a value ranging from 0 to 3 and such that x+y=3;

a compound of general formula (III):

wherein at least one of the groups R 5 and/or R 6 represent the compatibilizer C and represent independently of each other an aromatic cycle,

a compound of general formula (IV): R 7 —(COOH) z , wherein R 7 represents the compatibilizer C and z being an integer varying from 2 to 4,

a compound of general formula (V):

wherein the groups Y and/or Y′ represent independently of each other, a hydrogen atom or a group selected from the group consisting of: —(CH 2 ) q —CH 3 , —(CH 2 ) q —NH 2 , —(CH 2 ) q —OH, —(CH 2 ) q —COOH and

with q being an integer ranging from 2 to 18 and p being an integer greater than or equal to 2, with the proviso that Y and Y′ cannot represent the group —(CH 2 ) q —CH 3 simultaneously, and

a compound of general formula (VI): R 8 —NH—CO—CO—NH—R 9 , wherein R 8 and/or R 9 represent the compatibilizer C and represent independently of each other a linear hydrocarbon chain of at least 4 carbon atoms.

2. The method according to claim 1 , wherein the organogelator derivative is a compound of general formula (IV), wherein z is equal to 2 and R 7 represents a linear hydrocarbon chain comprising at least 4 carbon atoms.

3. The method according to claim 1 , wherein the organogelator derivative has a molar mass of less than or equal to 1,000 g·mol −1 .

4. The method according to claim 1 , wherein the bituminous composition comprises from 0.1 to 20% by mass of organogelator derivative.

5. The method according to claim 1 , wherein the bituminous composition further comprises at least one polymer.

6. The method according to claim 1 , wherein the bituminous composition comprises a cross-linking agent.

7. The method according to claim 1 , for improving the resistance to aggressive chemical agents of the bituminous composition when the latter is utilized in a roadway application as a surface layer or when the latter is mixed with aggregates in a bituminous mix.

8. The method according to claim 5 , wherein the polymer is a copolymer of a monovinylaromatic hydrocarbon and conjugate diene.

9. The method according to claim 8 , wherein the copolymer of a monovinylaromatic hydrocarbon and conjugate diene has a content of units with 1-2 double bonds units derived from the conjugate diene comprised between 5% and 50% by mass, based on the total mass of the conjugate diene units.

10. The method according to claim 1 , wherein the petroleum hydrocarbons are gasolines, kerosenes, gasoils, or mixtures thereof.

11. A method for improving resistance to petroleum hydrocarbons of a bituminous composition, the method comprising:

adding an organogelator derivative to a bitumen to generate a bituminous composition; and

contacting the bituminous composition with petroleum hydrocarbons,

wherein the organogelator derivative is selected from the group consisting of 2′,3-bis[[3-[3,5-di-tert-butyl-4-hydroxyphenyl]propionyl]]propionohydrazide, 1,3:2,4-di-O-benzylidene-D-sorbitol, 1,3:2,4-bis(p-chlorobenzylidene)sorbitol, sebacic acid, and combinations thereof.

12. The method according to claim 11 , wherein prior to contacting, the method comprises:

stirring the bitumen at 300 rpm and at a temperature of 185° C. in a reactor;

adding the organogelator derivative to the reactor containing the bitumen; and

stirring the bitumen and organogelator derivative at 300 rpm and at a temperature of 185° C. to generate the bituminous composition.

13. The method according to claim 12 , further comprising:

adding a diblock styrene and butadiene copolymer to the bitumen prior to adding the organogelator derivative.

14. The method according to claim 11 , wherein it takes form 8 to 24 hours for a 5 gram ball to move downward with the bituminous composition to a distance of 25 mm when the 5 gram ball is placed on a ring of the bituminous composition and the bituminous composition and ball are submerged in kerosene.

15. The method according to claim 11 , wherein the petroleum hydrocarbons are gasolines, kerosenes, gasoils, or mixtures thereof.