Fouling reduction in hydrochlorosilane production

1. A method for reducing fouling of a hydrogenation reactor in a hydrochlorosilane production plant comprising a silicon tetrachloride superheater having iron-containing walls and a hydrogenation reactor, the method comprising:

including at least 0.2 mol % of trichlorosilane in a silicon tetrachloride process stream comprising silicon tetrachloride and hydrogen in the silicon tetrachloride superheater having iron-containing walls, so as to inhibit HCl formation in the silicon tetrachloride superheater when operating at a temperature sufficient to cause a reaction between the silicon tetrachloride and the hydrogen to produce HCl in the absence of the at least 0.2 mol % of trichlorosilane, thereby inhibiting FeCl 2 formation by a reaction of HCl and iron in the iron-containing walls and transport of the FeCl 2 to the hydrogenation reactor, and thereby reducing iron silicide fouling of the hydrogenation reactor by inhibiting iron silicide formation by a reaction of the silicon tetrachloride, hydrogen, and the FeCl 2 that would be formed in the absence of the at least 0.2 mol % of trichlorosilane.

2. The method of claim 1 , wherein the at least 0.2 mol % of trichlorosilane is added to the silicon tetrachloride process stream upstream of the silicon tetrachloride superheater.

3. The method of claim 1 , wherein including the at least 0.2 mol % of trichlorosilane in the silicon tetrachloride process stream inhibits superheater corrosion by the HCl that would be produced in the absence of the at least 0.2 mol % of trichlorosilane.

4. The method of claim 1 , wherein the trichlorosilane is included at a concentration of from 0.2 mol % to 2 mol %.

5. The method of claim 1 , wherein the trichlorosilane is included at a concentration of from 0.5 mol % to 1.5 mol %.

6. The method of claim 1 , wherein the trichlorosilane is included at a concentration of from 0.9 mol % to 1.1 mol %.

7. The method of claim 1 , wherein the silicon tetrachloride process stream further comprises phosphine or other phosphorus-based compounds, and wherein including the at least 0.2 mol % of trichlorosilane further reduces iron phosphide fouling.

8. A method for inhibiting, during hydrochlorosilane production, corrosion of a silicon tetrachloride superheater in a hydrochlorosilane production plant comprising a silicon tetrachloride superheater having iron-containing walls and a hydrogenation reactor thereby reducing fouling of the hydrogenation reactor, the method comprising:

including from 0.2 mol % to 2 mol % of trichlorosilane in a process stream of the silicon tetrachloride superheater, the process stream comprising silicon tetrachloride and hydrogen,

wherein presence of the trichlorosilane in the process stream inhibits reaction of the silicon tetrachloride with the hydrogen at an operating temperature of the superheater thereby avoiding formation of HCl,

further wherein avoiding the formation of the HCl inhibits a corrosive reaction of HCl with the iron-containing walls of the superheater, in turn reducing formation of FeCl 2 and transport of the FeCl 2 to the hydrogenation reactor, and

further wherein reducing the formation of FeCl 2 and transport of the FeCl 2 to the hydrogenation reactor reduces iron silicide formation and associated iron silicide fouling of the hydrogenation reactor compared to iron silicide fouling produced by a process stream that does not comprise trichlorosilane.

9. The method of claim 8 , wherein including from 0.2 mol % to 2 mol % of trichlorosilane in the process stream comprises adding from 0.2 mol % to 2 mol % of trichlorosilane to the silicon tetrachloride process stream upstream of the silicon tetrachloride superheater.

10. The method of claim 8 , wherein the trichlorosilane is included at a concentration of from 0.5 mol % to 1.5 mol %.

11. The method of claim 8 , wherein the trichlorosilane is included at a concentration of from 0.9 mol % to 1.1 mol %.

12. The method of claim 8 , wherein the silicon tetrachloride process stream further contains phosphine or other phosphorus-based compounds, and wherein including from 0.2 mol % to 2 mol % of trichlorosilane in the process stream further reduces iron phosphide fouling compared to iron phosphide fouling that would be produced in the absence of the 0.2 mol % to 2 mol % of trichlorosilane.

13. The method of claim 8 , wherein iron silicide fouling is reduced at distributor orifices of a distributor plate in the hydrogenation reactor compared to iron silicide fouling that would be produced in the absence of the 0.2 mol % to 2 mol % of trichlorosilane.

14. The method of claim 12 wherein iron phosphide and iron silicide fouling is reduced at distributor orifices of a distributor plate in the hydrogenation reactor.

15. A method for reducing fouling of a hydrogenation reactor in a hydrochlorosilane production plant comprising a silicon tetrachloride superheater having iron-containing walls and a hydrogenation reactor, the method comprising:

including at least 0.2 mol % of trichlorosilane in a silicon tetrachloride process stream comprising silicon tetrachloride and hydrogen;

flowing the silicon tetrachloride process stream comprising the at least 0.2 mol % of trichlorosilane into the silicon tetrachloride superheater having iron-containing walls;

heating the silicon tetrachloride process stream comprising the at least 0.2 mol % of trichlorosilane in the silicon tetrachloride superheater to form a heated silicon tetrachloride process stream; and

subsequently flowing the heated silicon tetrachloride process stream into the hydrogenation reactor, wherein the heated silicon tetrachloride process stream is mixed with a hydrogen process stream.

16. The method of claim 15 , wherein including the at least 0.2 mol % trichlorosilane comprises adding at least 0.2 mol % trichlorosilane to the silicon tetrachloride process stream upstream of the silicon tetrachloride superheater.

17. The method of claim 15 , wherein the trichlorosilane is included at a concentration of from 0.2 mol % to 2 mol %.

18. The method of claim 15 , wherein the trichlorosilane is included at a concentration of from 0.5 mol % to 1.5 mol %.

19. The method of claim 15 , wherein the trichlorosilane is included at a concentration of from 0.9 mol % to 1.1 mol %.