A method for preparing a negative electrode material of a lithium ion battery is provided. In the method, a solvent-thermal reaction of a graphite material and a modifier precursor in an organic solvent is conducted to form a reaction product. And then, the reaction product is dried. Next, a heat treatment is applied to the dried reaction product to obtain the negative electrode material. The negative electrode material prepared by the method has improved cycle stability and high current performance.
1. A method for preparing a negative electrode material of a lithium ion battery, comprising:
conducting a solvothermal reaction of a graphite material and a modifier precursor in an organic solvent to form a reaction product, wherein the graphite material, the organic solvent and the modifier precursor are mixed and put into a sealing system to be heated to a constant reaction temperature to conduct the solvothermal reaction, wherein a reaction temperature of the solvothermal reaction is in a range from 140° C. to 200° C.;
drying the reaction product; and
applying a heat treatment to the dried reaction product to obtain a negative electrode material comprising a modifier.
2. The method of claim 1 , wherein the graphite material comprises at least one selected from a group consisting of graphitized meso-carbon microbead (MCMB), natural graphite and artificial graphite.
3. The method of claim 1 , wherein the modifier comprises at least one selected from a group consisting of aluminum oxide, titanium oxide, cobalt oxide, nickel oxide, silicon oxide, boron oxide, zirconium oxide and vanadium oxide.
4. The method of claim 1 , wherein the modifier precursor comprises at least one of an alkoxide and an oxyhydroxide, the alkoxide is at least one selected from a group consisting of aluminum alkoxide, titanium alkoxide, cobalt alkoxide, nickel alkoxide, silicon alkoxide, boron alkoxide, zirconium alkoxide and vanadium alkoxide, and the oxyhydroxide is at least one selected from a group consisting of aluminum oxyhydroxide, titanium oxyhydroxide, cobalt oxyhydroxide, nickel oxyhydroxide, silicon oxyhydroxide, boron oxyhydroxide, zirconium oxyhydroxide and vanadium oxyhydroxide.
5. The method of claim 1 , wherein the organic solvent comprises at least one selected from a group consisting of alcohols, alkanes, cycloalkanes, carbonates, benzene and benzene derivatives.
6. The method of claim 1 , wherein the organic solvent comprises at least one selected from a group consisting of anhydrous ethanol, isopropanol and N-methyl-2-pyrrolidone (NMP).
7. The method of claim 1 , wherein a reaction time of the solvothermal reaction is in a range from 1 hour to 24 hours.
8. The method of claim 1 , wherein a treatment temperature of the heat treatment is in a range from 250° C. to 900° C.
9. The method of claim 1 , wherein a weight ratio of the modifier to the negative electrode material is in a range from 0.05% to 20%.
10. The method of claim 1 , wherein a weight ratio of the modifier to the negative electrode material is in a range from 0.5% to 5%.