Granted Patent B2

US 9,790,629 · App. 13/680,380 · Granted Oct 17, 2017

Inventors: Gary W. Anderson (Lebanon, TN); Susannah D. Gelotte (Simpsonville, SC)

Assignee: Fiberweb, LLC

D06C3/06B29C47/0057B29C55/18B32B3/00B32B3/26B32B5/00B32B5/02B32B5/022B32B5/12B32B7/00B32B7/02B32B7/04B32B7/12B32B27/00B32B27/06B32B27/12B32B27/32B29C47/025B29C55/04B29C55/06B29C55/08B29C55/12B32B2255/00B32B2255/02B32B2262/00B32B2262/02B32B2262/0253B32B2307/54B32B2307/718B32B2307/724B32B2307/7265B32B2439/00B32B2571/00D01D5/088D01D5/098D01F6/04D01F6/06D04H3/005D04H3/08D04H13/001D04H13/003D04H13/007Y10T156/10Y10T428/24942Y10T428/249953Y10T428/249978Y10T442/2025Y10T442/2139Y10T442/2148Y10T442/2213Y10T442/2861Y10T442/674Y10T442/681

Abstract

Claims (13)

1. A method of preparing a composite sheet material having strength and barrier properties suitable for use as a housewrap, the method comprising:

cold-drawing substantially continuous filaments having a fiber birefringence of at least 0.022;

forming a spunbond nonwoven substrate comprising the substantially continuous filaments, the spunbond nonwoven substrate is area bonded with the substantially continuous filaments being bonded to one another at their crossover points;

extrusion coating a polyolefin film layer onto a surface of the spunbond nonwoven substrate to form a composite sheet material, the composite sheet material having a grab tensile strength of at least 178 Newtons in at least one of the machine direction (MD) or the cross-machine direction (CD), and

incrementally stretching the composite sheet in at least one of the CD and MD forming stretched zones separated by zones of substantially unstretched or less stretched material to impart to the composite a hydrostatic head of at least 100 cm, and a moisture vapor transmission rate (MVTR) of at least 35 g/m 2 /24 hr at 50% relative humidity and 23° C. to no more than about 132 g/m 2 /24 hr at 50% relative humidity and 23° C.

2. The method according to claim 1 , comprising passing the composite sheet material through a pair of intermeshing rolls configured for achieving stretching in the cross-direction (CD) of the composite sheet material.

3. The method according to claim 1 , comprising passing the composite sheet material through a pair of intermeshing rolls configured for stretching in the machine direction (MD) of the composite sheet material.

4. The method according to claim 1 , wherein the nonwoven substrate has basis weight of at least 50 g/m 2 and the composite sheet material has a grab tensile strength in both the machine direction (MD) and cross-machine direction (CD) of at least 178 Newtons.

5. The method according to claim 1 , wherein the polyolefin film layer extends uninterruptedly and continuously over the surface of the nonwoven substrate and is intimately bonded thereto to provide a peel adhesion of at least 150 grams per inch, the film layer comprising a polyolefin polymer and at least 40% by weight inorganic filler, the film layer having a basis weight of at least 25 g/m 2 , and the film layer defining an outer surface of the composite sheet material.

6. The method according to claim 1 , wherein the polyolefin film layer comprises at least 40% by weight of an inorganic filler.

7. The method according to claim 6 , wherein the composite sheet material has a Gurley porosity of at least 400 seconds and a basis weight of from 60 to 140 g/m 2 .

8. The method according to claim 1 , wherein the method comprises incrementally stretching the composite sheet in both the CD and MD.

9. The method according to claim 1 , wherein the composite sheet has a machine direction (MD) tensile elongation from about 37% to about 55% and a cross-machine direction (CD) tensile elongation from about 33% to about 56%.