Glass composition and its use in conductive silver paste
View Patent ↗A lead-tellurium-lithium-titanium-oxide glass composition is useful as a component of a conductive silver paste. Especially useful are P-containing and V-containing lead-tellurium-lithium-titanium-oxide glass composition. Conductive silver via paste comprising particulate conductive silver and any of the lead-tellurium-lithium-titanium-oxide glass compositions of the invention can be used in providing the metallization of the holes in the silicon wafers of MWT solar cells. The result is a metallic electrically conductive via between the collector lines on the front side and the emitter electrode on the back-side of the solar cell. The paste can also be used to form the collector lines on the front-side of the solar cell and the emitter electrode on the back-side of the solar cell.
1. A conductive silver paste comprising:
(a) silver,
(b) a glass composition consisting of at least 15 wt % but less than 25 wt % PbO, 50 to 75 wt % TeO 2 , 0.1 to 4 wt % Li 2 O, 0.25 to 5 wt % TiO 2 , and 3 to 12 wt % P 2 O 5 ; and
(c) an organic vehicle, wherein said silver and said glass composition aredispersed in said organic vehicle.
2. The conductive silver paste of claim 1 , wherein said glass composition consists of at least 20 wt % but less than 25 wt % PbO, 55 to 75 wt % TeO 2 , 0.5 to 2.5 wt % Li 2 O, 0.5 to 3 wt % TiO 2 and 3 to 9 wt % P 2 O 5 .
3. A glass composition consisting of at least 15 wt % but less than 25 wt % PbO, 45 to 65 wt % TeO 2 , 0.1 to 4 wt % TiO 2 , 0.25 to 5 wt % TiO 2 and 10 to 30 wt % V 2 O 5 .
4. The glass composition of claim 3 , said glass composition consisting of at least 20 wt % but less than 25 wt % PbO, 45 to 60 wt % TeO 2 , 0.5 to 2.5 wt % Li 2 O, 0.5 to 3 wt % TiO 2 and 15 to 25 wt % V 2 O 5 .
5. A conductive silver paste comprising:
(a) silver;
(b) a glass composition of claim 3 or 4 ; and
(c) an organic vehicle, wherein said silver and said glass composition are dispersed in said organic vehicle.
6. The conductive silver paste of claim 5 , wherein said silver is in the form of silver particles.
7. The conductive silver paste of claim 6 , wherein said silver particles are spherical.
8. The conductive silver paste of claim 7 , wherein said spherical silver particles have a surface coating of surfactant.
9. The conductive silver paste of claim 8 , wherein said surface coating of surfactant is a diethylene glycol coating.
10. The conductive silver paste of claim 7 , said spherical silver particles having a d 50 of from 1.7 to 1.9 μm and a d 10 ≧1 μm and a d 90 ≦3.8 μm.
11. The conductive silver paste of claim 5 , wherein said silver is in the form of irregular particles having a d 50 of from 5.4 to 11.0 μm.
12. The conductive silver paste of claim 6 , wherein said silver particles are in flake form.
13. The conductive silver paste of claim 5 , said conductive silver paste comprising 80-90 wt % silver and 0.2 to 2.0 wt % glass composition, based on the total weight of the conductive silver paste.
14. The conductive silver paste of claim 13 , said conductive silver paste comprising 85-90 wt % silver.
15. A metal-wrap-through silicon solar cell with an n-type or a p-type silicon base comprising the fired conductive silver paste of claim 5 .