Set retardant for hydraulic cement compositions and admixtures therefor
A zinc-oxide based set retardant additive and admixture for use in Portland cement or other hydraulic cement mixtures. The admixture may comprise silica fume, vitreous calcium aluminosilicate, magnesium aluminum silicate hydrate, a cellulose ether derivative, or their equivalents. The zinc-oxide based set retardant may be interground or pre-blended, pre-packaged, or added on the jobsite, as an admixture, additive, or addition. The zinc-based set retardant may be subsequently added or mixed into a ready mix or wet mixture of portland cement or other hydraulic cement, sand and/or aggregate, with or without fillers, and water, with or without other pozzolans or polymers.
1. A hydraulic cement composition that achieves a set time of between about 2 to about 5 hours, comprising:
about 50 wt % to about 75 wt % of a hydraulic cement mixture;
about 0.01 wt % to about 2 wt % zinc oxide;
about 5 wt % to about 45 wt % of one or more pozzolans; and
about 0.01 wt % to about 2 wt % cellulosic polymer.
2. The hydraulic cement composition of claim 1 , wherein the zinc oxide comprises about 0.01 wt % to about 0.25 wt %.
3. The hydraulic cement composition of claim 1 , wherein the zinc oxide comprises at least one of acicular zinc oxide powder and spherical or globular zinc oxide powder.
4. The hydraulic cement composition of claim 1 , wherein the hydraulic cement mixture comprises hydraulic cement and sand.
5. The hydraulic cement composition of claim 4 , wherein:
the hydraulic cement mixture comprises about 40 wt % of white cement and about 60 wt % of marble sand; and
the zinc oxide comprises at least 95% of zinc oxide powder smaller than about 325 mesh (45 micron).
6. The hydraulic cement composition of claim 5 , wherein the zinc oxide comprises at least 95% of zinc oxide powder smaller than about 200 mesh (75 micron).
7. The hydraulic cement composition of claim 1 , wherein the zinc oxide comprises an acicular zinc oxide powder containing at least about 95% of zinc oxide grounded smaller than about 325 mesh (45 micron).
8. The hydraulic cement composition of claim 1 , wherein the one or more pozzolans comprise at least one of silica fume, fly ash, calcined kaolin, and vitreous calcium aluminosilicate.
9. The hydraulic cement composition of claim 8 , wherein the one or more pozzolans comprise about 0 wt % to about 30 wt % silica fume, about 0 wt % to about 45 wt % fly ash, and about 0 wt % to about 40 wt % vitreous calcium aluminosilicate.
10. The hydraulic cement composition of claim 1 , wherein the one or more pozzolans comprise about 1 wt % to about 15 wt % silica fume, about 3 wt % to about 27 wt % fly ash, and about 5 wt % to about 27 wt % vitreous calcium aluminosilicate or calcined kaolin.
11. The hydraulic cement composition of claim 1 , wherein the one or more pozzolans comprise about 10 wt % to about 20 wt % of calcined clay, about 5 wt % to about 15 wt % of ultra-fine fly ash, and about 4 wt % to about 7 wt % of fused silica, and the cellulosic polymer comprises less than 1 wt % of hydrooxyethylcellulose.
12. A method of preparing hydraulic cement achieving a set time of between 2 to 5 hours, comprising blending about 0.01 wt % to about 2 wt % zinc oxide, about 5 wt % to about 45 wt % of one or more pozzolans, about 0.01 wt % to about 2 wt % cellulosic polymer and about 50 wt % to about 75 wt % of a hydraulic cement mixture.
13. The method of claim 12 , wherein blending comprises blending the zinc oxide in an amount of about 0.01 wt % to about 0.25 wt %.
14. The method of claim 12 , wherein blending comprises blending the zinc oxide as acicular zinc oxide powder or as spherical or globular zinc oxide powder.
15. The method of claim 12 , wherein the hydraulic cement mixture comprises hydraulic cement and sand.
16. The method of claim 12 , wherein blending comprises pre-blending the zinc oxide, the one or more pozzolans and the cellulosic polymer as a set retarder and blending the set retarder and the hydraulic cement mixture when the set retarder is at a temperature of between about 70° F. and about 120° F.
17. The method of claim 12 , wherein blending comprises blending the zinc oxide by combining at least 95% zinc oxide powder smaller than about 325 mesh (45 micron), and blending the hydraulic cement mixture comprises blending about 40 wt % of white cement and about 60 wt % of marble sand.
18. The method of claim 12 , wherein blending comprises blending the one or more pozzolans as at least one of silica fume, fly ash, calcined kaolin and vitreous calcium aluminosilicate.
19. The method of claim 18 , wherein blending comprises blending the one or more pozzolans by combining about 0 wt % to about 30 wt % silica fume, about 0 wt % to about 45 wt % fly ash, and about 0 wt % to about 40 wt % calcined kaolin or vitreous calcium aluminosilicate.
20. The method of claim 18 , wherein blending comprises blending the one or more pozzolans as about 1 wt % to about 15 wt % silica fume, about 3 wt % to about 27 wt % fly ash, and about 5 wt % to about 27 wt % calcined kaolin or vitreous calcium aluminosilicate.