Self-adhesive laminate and method of making it
A decorative laminate includes a laminate substrate coated with an adhesive layer. The adhesive layer is a layer of a physically setting, solvent-free adhesive material including an acrylic polymer. The adhesive layer is self-adhesive at room temperature. The adhesive-coated laminate substrate has a peeling-off force of at least 0.2 N/mm 2 , after application on a carrier. A method for the production of the adhesive-coated laminate substrate, its use as a coating material, and a composite of the adhesive-coated laminate substrate and a carrier material are also provided.
1. A high pressure decorative laminate, comprising in adjacent sequence:
a hardened high pressure decorative laminate substrate having a homogeneously closed structure and a density not less than about 1.35 grams per cubic centimeter, consisting of layers of fibrous strips impregnated with a cured resin and one or more decorative paper layers impregnated with a resin;
an adhesive layer including a physically setting, solvent-free terpolymer of vinyl acetate-ethylene and acrylic, positioned adjacent to the hardened high pressure decorative laminate substrate; and
a release layer including a siliconized paper or film positioned adjacent to the adhesive layer.
2. The high pressure decorative laminate of claim 1 , wherein the adhesive layer is self-adhesive at room temperature.
3. The high pressure decorative laminate of claim 1 , wherein the cured resin comprises at least one of a melamine resin, an epoxy resin, a phenoplastic, and a urea-formaldehyde resin.
4. The high pressure decorative laminate of claim 3 , wherein the cured resin comprises a melamine resin.
5. The high pressure decorative laminate of claim 1 , wherein the fibrous strips comprise cellulose strips.
6. The high pressure decorative laminate of claim 1 , wherein the adhesive layer comprises a non-pressure sensitive adhesive layer adjacent to the hardened high pressure decorative laminate substrate and a self-adhesive layer adjacent to the non-pressure sensitive adhesive layer, the self-adhesive layer including the physically setting, solvent-free terpolymer of vinyl acetate-ethylene and acrylic.
7. The high pressure decorative laminate of claim 6 , wherein the self-adhesive layer further comprises an elastomer.
8. The high pressure decorative laminate of claim 7 , wherein the elastomer comprises high molecular weight polyisobutylene rubber having a number-average molecular weight of about 300,000 to about 3,500,000 grams/mol.
9. The high pressure decorative laminate of claim 6 , wherein the non-pressure sensitive adhesive layer comprises polyvinyl acetate.
10. The high pressure decorative laminate of claim 1 , wherein the layers of fibrous strips impregnated with a cured resin are bonded together under heat and high pressure of about 5 mPa or greater.
11. The high pressure decorative laminate of claim 10 , wherein the fibrous strips impregnated with a cured resin are bonded together at a temperature of about 120° C. to about 150° C. and a pressure of about 7 mPa or greater.
12. The high pressure decorative laminate of claim 1 , wherein the adhesive layer comprises, based on dry weight, about 10 to about 70% by weight of an elastomer, about 10 to about 70% by weight of the terpolymer of vinyl acetate-ethylene and acrylic, about 15 to about 40% by weight of a plasticizer, and about 15 to about 30% by weight of a hydrocarbon resin.
13. The high pressure decorative laminate of claim 12 , wherein the plasticizer comprises a low molecular weight polyisobutylene having a molecular weight of about 800 to about 5000 grams/mol.
14. The high pressure decorative laminate of claim 12 , wherein the elastomer comprises a block copolymer having two end blocks of a vinyl aromatic monomer and at least one middle block that contains a conjugated diene or is formed from an ethylene-butylene copolymer or an ethylene-propylene copolymer.
15. The high pressure decorative laminate of claim 14 , wherein the end blocks have a molecular weight of about 6000 to about 60,000 grams/mol and the middle block has a molecular weight of about 30,000 to about 150,000 grams/mol.
16. The high pressure decorative laminate of claim 12 , wherein the hydrocarbon resin is selected from the group consisting of gum resin, wood resin, tallow oil resin, distillate resin, hydrogenated resin, dimerized resin, polymerized resin, and combinations thereof.