Method for manufacturing nanowire meshes
A variety of methods, devices, systems and arrangements are implemented involving nanowire meshes. One such method is implemented to include synthesizing metal nanowires in a solution containing a structure-directing agent. The metal nanowires are deposited on a substrate to form a sheet of nanowires. The deposited metal nanowires are heated to a temperature less than about 200 degrees Celsius and for a period of time of about 10 minutes to 60 minutes, thereby removing the structure-directing agent and modifying the electrical conductivity and optical transmittance of the sheet of nanowires.
1. A method comprising:
synthesizing nanowires containing silver in a solution containing a structure-directing agent;
forming a sheet of nanowires from the synthesizing nanowires; and
heating the sheet of nanowires at a temperature and for a time sufficient to remove the structure-directing agent and to produce a sheet conductivity level, for the sheet of nanowires, that is less than 25 ohms per square and a sheet transmittance, for the sheet of nanowires, of at least about 80% for all wavelengths between about 400 nanometers and 800 nanometers.
2. The method of claim 1 , wherein the step of heating includes heating the sheet of nanowires to a temperature of between 180-200 degrees (Celsius) for 18-22 minutes, and results in the sheet conductivity level being less than 15 ohms per square and sheet transmittance of at least 80% for all wavelengths between 400 nanometers and 800 nanometers.
3. The method of claim 1 , wherein the step of heating results in sheet transmittance of at least about 88% for all wavelengths between about 400 nanometers and 800 nanometers, further including applying a metallic coating to the nanowires.
4. The method of claim 1 , wherein the step of synthesizing nanowires includes creating predominantly silver nanowires having an average length of about 5 μm to 20 μm and an average diameter of less than about 100 nm.
5. The method of claim 1 , wherein the step of synthesizing nanowires includes creating predominantly silver nanowires having an average length of about 8 μm to 9 μm and an average diameter of less than of about 100 nm.
6. The method of claim 1 , further including a step of immersing the sheet of nanowires in a solution of gold salt (HAuCl4) to effect a replacement of at least some of the silver in the nanowire with gold.
7. The method of claim 6 , further including a step of heating the immersed sheet of nanowires at temperatures between 25 degrees and 100 degrees (Celsius) for 1 to 10 minutes.
8. The method of claim 6 , further including a step of selecting an immersion time as a function of a desired ratio of gold to silver.
9. The method of claim 6 , wherein processing parameters for the step of immersing is controlled to form a thin shell of gold on the sheet of nanowires.
10. The method of claim 1 , further including a step of depositing an organic photovoltaic cell onto the sheet of nanowires.
11. The method of claim 1 , further including a step of applying, to the heated and deposited silver nanowires, pressure of about 1.4(+/−0.6)×10e4 pounds per square inch for about 30 seconds.
12. The method of claim 1 , further including a step of applying uni-axial pressure to the sheet of heated nanowires to reduce surface roughness of the sheet of nanowires.
13. The method of claim 1 , wherein the sheet of nanowires exhibits resistance that is greater than 1 kΩ/sq prior to heating.
14. The method of claim 1 , wherein the sheet of nanowires exhibits resistance that is approximately 100 Ω/sq after the step of heating.
15. The method of claim 1 , further comprising:
providing a substrate; and wherein the step of heating results in a silver nanowire mesh located on the substrate and having a sheet conductivity level that is less than 25 ohms per square and a sheet transmittance of at least 80% for all wavelengths between about 400 nanometers and 800 nanometers.
16. The method of claim 15 , further including small molecular weight organic photovoltaic cells located on the silver nanowire mesh.
17. The method of claim 15 , wherein the silver nanowire mesh includes a poly(ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT:PSS) layer.
18. The method of claim 17 , further including a bilayer solar cell located on the silver nanowire mesh.
19. The method of claim 18 , wherein the bilayer solar cell includes a layer structure of copper phthalocyanine (CuPc), perylenetetracarboxylix bisbenzimidazole (PTCBI) and of bathocuproine (BCP).