PROTECTIVE SUIT FABRIC AND SPUN YARN USED FOR THE SAME
A heat-resistant flame-retardant protective suit fabric of the present invention is formed of a uniform blended spun yarn including 25 to 75 mass % of polyetherimide fiber, 20 to 50 mass % of at least one fiber selected from wool and flame-retardant rayon, and 5 to 25 mass % of para-aramid fiber when the spun yarn is 100 mass %. The fabric experiences no heat shrinkage when exposed to a heat flux at 80 kW/m 2 ±5% for 3 seconds in accordance with ISO 9151 Determination of Heat Transmission on Exposure to Flame. And the char length is not more than 10 cm in the longitudinal and horizontal directions in the flammability test specified in JIS L 1091A-4. Thereby, the present invention provides a protective suit fabric that provides comfort in wearing even if the suit is worn in the hot seasons or even if the wearer perspires during exertion. The fabric has high heat resistance and high flame retardance, favorable dye affinity, and the fabric can be produced at a low cost. The present invention provides also a spun yarn used for the fabric.
1 . A heat-resistant flame-retardant protective suit fabric formed of a uniform blended spun yarn comprising 25 to 75 mass % of polyetherimide fiber, 20 to 50 mass % of at least one fiber selected from wool and flame-retardant rayon, and 5 to 25 mass % of para-aramid fiber when the spun yarn is 100 mass %,
wherein the fabric experiences no heat shrinkage when exposed to a heat flux at 80 kW/m 2 ±5% for 3 seconds in accordance with ISO 9151 Determination of Heat Transmission on Exposure to Flame, and
the char length is not more than 10 cm in the longitudinal and horizontal directions in the flammability test specified in JIS L 1091A-4.
2 . The protective suit fabric according to claim 1 , wherein the uniform blended spun yarn is formed of a two-fold yarn, a twist factor Ks 1 of a single yarn is in a range of 2560 to 2750, the two-fold yarn is twisted in a direction opposite to the direction for twisting the single yarn, and a twist factor K S2 of the two-fold yarn is in a range of 3490 to 3760,
where the twist factor Ks 1 of the single yarn and the twist factor Ks 2 of the two-fold yarn are calculated by equations below:
Ks 1 =T 1 ·√S 1
Ks 2 =T 2 ·√S 2
in the equations, T 1 indicates a twist number (time/m) of the single yarn, T 2 indicates a twist number (time/m) of the two-fold yarn, S 1 indicates a single yarn fineness (tex) and S 2 indicates a two-fold yarn fineness (tex).
3 . The protective suit fabric according to claim 1 , wherein the blended spun yarn further comprises an antistatic fiber.)
4 . The protective suit fabric according to claim 1 , which is either a knitted fabric or a woven fabric.
5 . The protective suit fabric according to claim 1 , wherein the polyetherimide fiber that forms the protective suit fabric has been dyed as a fiber, as a yarn or as a fabric, and the para-aramid fiber has been spun-dyed.
6 . The protective suit fabric according to claim 1 , wherein the uniform blended spun yarn comprises 25 to 74 mass % of polyetherimide fiber, 20 to 50 mass % of at least one fiber selected from wool and flame-retardant rayon, 5 to 25 mass % of para-aramid fiber, and 0.1 to 1 mass % of antistatic fiber.
7 . The protective suit fabric according to claim 1 , wherein the mass per unit of the protective suit fabric is in a range of 100 to 340 g/m 2 .
8 . A spun yarn used for a heat-resistant flame-retardant protective suit fabric,
wherein the spun yarn is a uniform blended spun yarn comprising 25 to 75 mass % of polyetherimide fiber, 20 to 50 mass % of at least one fiber selected from wool and flame-retardant rayon, and 5 to 25 mass % of para-aramid fiber when the spun yarn is 100 mass %.
9 . The spun yarn according to claim 8 , wherein the spun yarn is formed of a two-fold yarn, a twist factor Ks 1 of a single yarn is in a range of 2560 to 2750, the two-fold yarn is twisted in a direction opposite to the direction for twisting the single yarn, and a twist factor K S2 of the two-fold yarn is in a range of 3490 to 3760,
where the twist factor Ks 1 of the single yarn and the twist factor Ks 2 of the two-fold yarn are calculated by equations below:
Ks 1 =T 1 ·√S 1
Ks 2 =T 2 ·√S 2
in the equations, T 1 indicates a twist number (time/m) of the single yarn, T 2 indicates a twist number (time/m) of the two-fold yarn, S 1 indicates a single yarn fineness (tex) and S 2 indicates a two-fold yarn fineness (tex).
10 . The spun yarn according to claim 8 , wherein the blended spun yarn further comprises an antistatic fiber.
11 . The spun yarn according to claim 10 , wherein the content of the antistatic fiber is in a range of 0.1 to 1 mass %.