Reactive isocyanate-terminated prepolymers for binder applications
Elastomer composites are prepared by wetting particles of a natural or synthetic rubber with a liquid one-component moisture-curable resin composition and then exposing the wetted particles to moisture to cure the resin composition. The moisture-curable resin composition comprises (a) an isocyanate-terminated polyurethane prepolymer having an isocyanate content of from 0.5 to 12% by weight and (b) from 1 to 30%, based on the combined weight of components (a) and (b), of an epoxide or lactone compound having a molecular weight of from about 70 to about 1000 and which is miscible in the prepolymer at the relative proportions thereof that are present. In addition, the composition contains no more than 0.1% by weight of compounds having a primary or secondary amino group.
1. A process for preparing an elastomeric composite, comprising wetting particles of a natural or synthetic rubber with a liquid one-component moisture-curable resin composition and then exposing the wetted particles to moisture under conditions that the resin composition cures to form a binder phase which adheres the rubber particles together, wherein the moisture-curable resin composition comprises (a) an isocyanate-terminated polyurethane prepolymer having an isocyanate content of from 0.5 to 12% by weight and (b) from 1 to 30%, based on the combined weight of components (a) and (b), of an epoxide compound having a molecular weight of from about 70 to about 1000 and which is miscible in the prepolymer at the relative proportions thereof that are present, the composition containing no more than 0.1% by weight of compounds having a primary or secondary amino group and containing no more than 1% by weight of compounds that contain hydroxyl or thiol groups.
2. The process of claim 1 , wherein the prepolymer has an isocyanate content of from 3 to 10% by weight.
3. The process of claim 2 , wherein the epoxide compound has a molecular weight of from 85 to 300.
4. The process of claim 3 , wherein the epoxide compound has a molecular weight of from 85 to 200.
5. The process of claim 2 , wherein the moisture-curable resin composition contains from 2 to 10% by weight of the epoxide compound.
6. The process of claim 5 , wherein the moisture-curable resin composition contains from 2 to 5% by weight of the epoxide compound.
7. The process of claim 2 , wherein the epoxide compound is a glycidyl ether of an aliphatic, cycloaliphatic or aliphatic monol or polyol that contains from 2 to 20 carbon atoms.
8. The process of claim 7 , wherein the epoxide compound is butanediol diglycidyl ether, butane diol monoglycidyl ether, 1,2- or 1,3-propane diol diglycidyl ether or 1,2- or 1,3-propane diol monoglycidyl ether.
9. The process of claim 2 , wherein the elastomeric particles are wetted with the moisture-curable composition and then spread upon the ground, leveled and smoothed, and then allowed to cure at ambient temperature.
10. The process of claim 2 , wherein the particles are wetted with the moisture-curable composition and transferred to a drum mold, liquid water or steam is added to the wetted particles, and the curing step is performed in the drum mold.
11. A one-component binder composition comprising an isocyanate-terminated polyurethane prepolymer having an isocyanate content of from 3 to 10% by weight having dissolved therein (b) from 1 to 30%, based on the weight of the prepolymer, of a glycidyl ether of an aliphatic, cycloaliphatic or aliphatic monol or polyol that contains from 2 to 20 carbon atoms having a molecular weight of from about 70 to about 1000, the composition containing no more than 0.1% by weight of compounds having a primary or secondary amino group and containing no more than 1% by weight of compounds that contain hydroxyl or thiol groups.
12. The binder composition of claim 11 , wherein the epoxide compound has a molecular weight of from 85 to 300.
13. The binder composition of claim 12 , wherein the epoxide compound has a molecular weight of from 85 to 200.
14. The binder composition of claim 11 , wherein the moisture-curable resin composition contains from 2 to 10% by weight of the epoxide compound.
15. The binder composition of claim 14 , wherein the moisture-curable resin composition contains from 2 to 5% by weight of the epoxide compound.
16. The binder composition of claim 11 , wherein the epoxide compound is butanediol diglycidyl ether, butane diol monoglycidyl ether, 1,2- or 1,3-propane diol diglycidyl ether or 1,2- or 1,3-propane diol monoglycidyl ether.