Scattering film for organic EL, and organic EL light-emitting device equipped with same
Disclosed is a scattering film which can be used in an organic EL light-emitting device, in which the light utilization efficiency and field-of-view dependence, which have been problems so far in organic EL light-emitting devices, can be improved without interfering the two properties with each other. Specifically disclosed is a scattering film for an organic EL, which can be placed on the light emission surface side of an organic EL light-emitting device for use, and involves a scattering layer, wherein the scattering layer comprises a binder resin, microparticles having a different refractive index from that of the binder resin, and resin particles having a larger average particle diameter than that of the microparticles. The content of the microparticles is preferably 5 to 90 parts by weight relative to 100 parts by weight of the binder resin, and the content of the resin particles is preferably 100 to 300 parts by weight relative to 100 parts by weight of the binder resin.
1. A scattering film to be used in an organic EL light-emitting device, the scattering film including a scattering layer that contains:
binder resin;
microparticles having a different refractive index from the binder resin; and
resin particles having a larger average particle diameter than the microparticles, wherein
the microparticles include zirconium oxide particles and the content of the microparticles is 5 to 90 parts by weight per 100 parts of the binder resin,
the resin particles include silicone resin particles and the content of the resin particles is 100 to 300 parts by weight per 100 parts by weight of the binder resin, and
the scattering film is disposed on the side of a light-emitting surface of the organic EL light-emitting device.
2. The scattering film for organic EL according to claim 1 ,
wherein the average particle diameter of the microparticles is 1 μm or smaller and the average particle diameter of the resin particles is 1 μm or larger.
3. The scattering film for organic EL according to claim 1 , wherein the resin particles are silicone resin particles.
4. The scattering film for organic EL according to claim 1 , wherein the microparticles are inorganic particles.
5. The scattering film for organic EL according to claim 4 , wherein the inorganic particles are zirconium oxide particles.
6. An organic EL light-emitting device comprising:
a pair of electrodes;
an organic light-emitting layer provided between the pair of electrodes; and
a scattering layer provided on a light emission surface of the light-emission-side electrode of the pair of electrodes,
wherein the scattering layer contains binder resin, microparticles having a different refractive index from the binder resin, and resin particles having a larger average particle diameter than the microparticles; and wherein
the microparticles include zirconium oxide particles and the content of the microparticles is 5 to 90 parts by weight per 100 parts of the binder resin,
the resin particles include silicone resin particles and the content of the resin particles is 100 to 300 parts by weight per 100 parts by weight of the binder resin.
7. A scattering film to be used in an organic EL light-emitting device, the scattering film including a scattering layer that comprises:
a binder resin;
zirconium oxide microparticles having a different refractive index from the binder resin and the content of the zirconium oxide microparticles is 5 to 90 parts by weight per 100 parts of the binder resin; and
silicone resin particles having a larger average particle diameter than the microparticles, the silicone resin particles is 100 to 300 parts by weight per 100 parts by weight of the binder resin, and
the scattering film is disposed on the side of a light-emitting surface of the organic EL light-emitting device.
8. The scattering film for organic EL according to claim 7 ,
wherein the average particle diameter of the microparticles is 1 μm or smaller and the average particle diameter of the resin particles is 1 μm or larger.
9. The scattering film of claim 7 , wherein the refractive index of the resin particles is 1.3 to 1.6, the refractive index of the resin binder is 1.4 to 1.65 and the particle size of the resin particles are within the range of from 1 to 8 μm.
10. The scattering film of claim 7 wherein the difference in refractive index between the microparticles and the resin binder is 0.03 or larger.
11. The scattering film of claim 1 wherein the difference in refractive index between the microparticles and the resin binder is 0.03 or larger.