Synthesis of ultrasmall metal oxide nanoparticles
The invention generally relates to the ultrasmall MO x nanoparticles that are made in a solvothermal method using water soluble inorganic ammonium salt precursors of the MO x and organic amines, and slow heating to generate uniform ultrasmall MO x nanoparticles of 5 nm or less, as well as methods to make and use same.
1. A method of making ultrasmall metal oxide nanoparticles, comprising;
a) placing water soluble, inorganic ammonium oxometalate precursor in a reactor;
b) adding an excess of amine surfactant to said reactor,
c) optionally adding diols or amine oxides to said reactor;
d) heating the reactor until the ammonium oxometalate precursor structure collapses and the nucleation stage generates ultrasmall metal oxide nanoparticles of average size ≦5 nm.
2. The method of claim 1 , wherein the ultrasmall metal oxide nanoparticles have about 20-50 metal atoms per nanoparticle.
3. The method of claim 1 wherein the ammonium oxometalate precursor is selected from the group consisting of ammonium metatungstate, ammonium paratungstate, phosphotungstic acid hydrate, ammonium metamolybdate tetrahydrate, ammonium metavanadate, ammonium pentaborate octahydrate, ammonium hexachloroosmate(IV), ammonium chromate, ammonium perrhenate, ammonium dihydrogenphosphate, ammonium phosphomolybdate hydrate, ammonium hexachloroiridate(IV), ammonium tetrathiomolybdate, ammonium hexachloropalladate(IV), ammonium hexachlororhodate(III), and ammonium dichromate.
4. The method of claim 1 , wherein the metal oxide is WO x , MoO x , VO x or a doped variation of WO x , MoO x , and VO x .
5. The method of claim 1 , wherein the amine surfactant is oleylamine.
6. An ultrasmall metal oxide nanoparticle, produced by the method of claim 1 .
7. A method of making ultrasmall metal oxide nanoparticles, comprising;
a) placing 1 part of water soluble, inorganic ammonium oxometalate precursor, which is fully oxidized and has structural stability up to about 250° C., in a reactor;
b) adding 14-20 parts of oleylamine to said reactor,
c) optionally adding 0-1 part 1,12-dodecandiol or 0-1 part of trimethylamine N-oxide (TANO) to said reactor;
d) slowly heating the reactor at about 2° C./min while stirring under oxygen free conditions until the reactor reaches about 250-270° C.;
e) holding the reactor temperature at about 250-270° C. for 1-3hours until the ammonium oxometalate precursor structure collapses and the nucleation stage generates ultrasmall metal oxide nanoparticles of average size <5 nm and with about 20-40 metal atoms per nanoparticle.
8. The method of claim 7 further comprising: cooling the reactor to about room temperature and collecting said nanoparticles.
9. The method of claim 7 further comprising: precipitating the nanoparticles.
10. A method of claim 9 , wherein precipitation is caused by acetone or ethanol or methanol-chloroform.
11. The method of claim 7 , wherein the ammonium oxometalate precursor is selected from the group consisting of ammonium metatungstate, ammonium paratungstate, phosphotungstic acid hydrate, ammonium metamolybdate tetrahydrate, ammonium metavanadate, ammonium pentaborate octahydrate, ammonium hexachloroosmate(IV), ammonium chromate, ammonium perrhenate, ammonium dihydrogenphosphate, ammonium phosphomolybdate hydrate, ammonium hexachloroiridate(IV), ammonium tetrathiomolybdate, ammonium hexachloropalladate(IV), ammonium hexachlororhodate(III), and ammonium dichromate.
12. The method of claim 7 , wherein the synthesis includes 0.5 part of 1,12-dodecandiol and the nanoparticles increase to rod-shapes of about 3-7 nm×20-60 nm.
13. The method of claim 7 , wherein the synthesis includes 0.5 part of TANO and the nanoparticle size is 0.8-1.2 nm.
14. The method of claim 7 , wherein the metal oxide is WO x , MoO x , VO x or a doped variation of WO x , MoO x , and VO x .
15. The method of claim 7 , wherein the average nanoparticle size is ≦2 nm with a relative standard deviation of <10%.
16. A WO x , MoO x , VO x nanoparticle composition, wherein said WO x , MoO x , VO x nanoparticles or doped variations thereof are of size ≦5 nm with a relative standard deviation of <10%.
17. The WO x , MoO x , VO x nanoparticle composition of claim 16 , wherein said WO x , MoO x , VO x nanoparticles or doped variations thereof are of size about 2 nm with a relative standard deviation of <10%.
18. The WO x , MoO x , VO x nanoparticle composition of claim 16 , wherein said WO x , MoO x , VO x nanoparticles or doped variations thereof are of size about 1 nm with a relative standard deviation of <10%.
19. A catalyst, comprising WO x , MoO x , VO X nanoparticles or doped variations thereof that are of size ≦5 nm with a relative standard deviation of <10% bound to a solid support.
20. The catalyst of claim 19 , wherein said WO x , MoO x , VO x nanoparticles or doped variations thereof that are of size ≦2 nm with a relative standard deviation of <10%.
21. The catalyst of claim 19 , wherein said WO x , MoO x , VO x nanoparticles or doped variations thereof that are of size ≦1 nm with a relative standard deviation of <10%.
22. A method comprising utilizing the catalyst of claim 19 in a metathesis reaction.