Substrate coating on one or more sides

1. A method for coating one or more sides of substrates with catalytically active material, comprising material deposition under vacuum in a vacuum chamber, wherein the following steps are performed:

loading the vacuum chamber with at least one substrate,

closing and evacuating the vacuum chamber,

cleaning the substrate by introducing a gaseous reducing agent into the vacuum chamber,

removing the gaseous reducing agent,

applying an intermediate layer by means of vacuum arc deposition, wherein a substrate comprising the same material as the intermediate layer is introduced into the vacuum chamber,

applying a coating by means of vacuum arc deposition at a temperature of 150° C. to 400° C., wherein at least one metal taken from the group of ruthenium, iridium, titanium and mixtures thereof is introduced into the vacuum chamber and oxygen is supplied throughout the coating period,

in a last step the vacuum chamber is re-flooded and the coated substrate is removed from the chamber;

wherein the above steps and transitions from one step to the next are performed under vacuum which is set by means of a protective gas,

wherein migration of atoms from the intermediate layer into an outer layer of the coating on the intermediate layer is avoided, and

wherein at least 99% of the intermediate layer on one or more sides is kept free of constituents initially contained in the substrate, wherein at least 99% of the intermediate layer is kept free of non-oxidised metals; and

wherein a substrate coating, consisting of the intermediate layer and the coating applied to it, has a layer thickness of 1.5 to 2.5 μm.

2. The substrate coating method according to claim 1 , wherein the intermediate layer is completely kept free of constituents initially contained in the substrate and the coating applied onto the intermediate layer is completely kept free of non-oxidised metals.

3. The substrate coating method according to claim 1 , wherein the substrate is selected from a group comprising stainless steel and elements of the nickel group as well as coated stainless steel from elements of the nickel group.

4. The substrate coating method according to claim 1 , wherein the coating applied onto the intermediate layer consists of ruthenium dioxide.

5. The substrate coating method according to claim 1 , wherein the coating applied onto the intermediate layer is made up of a mixture of the metal oxides of ruthenium dioxide:iridium dioxide:titanium dioxide.

6. The substrate coating method according to claim 1 , wherein the intermediate layer features uneven areas on its surface.

7. The substrate coating method according to claim 1 , wherein the coating applied onto the intermediate layer features uneven areas on its surface.

8. A substrate comprising a substrate coating on one or more sides of the substrate, the substrate coating comprising an intermediate layer and a coating on the intermediate layer, the substrate prepared by a process comprising material deposition under vacuum in a vacuum chamber avoiding migration of atoms from the intermediate layer into an outer layer of the coating on the intermediate layer, wherein the following steps are performed:

loading the vacuum chamber with at least one substrate,

closing and evacuating the vacuum chamber,

cleaning the substrate by introducing a gaseous reducing agent into the vacuum chamber,

removing the gaseous reducing agent,

applying an intermediate layer by vacuum arc deposition, wherein a substrate comprising the same material of the intermediate layer is introduced into the vacuum chamber,

applying a coating by vacuum arc deposition at a temperature of 150° C. to 400° C.,

wherein at least one metal taken from the group of ruthenium, iridium, titanium and mixtures thereof is introduced into the vacuum chamber and oxygen is supplied throughout the coating period, and

in a last step the vacuum chamber is re-flooded and the substrate comprising the substrate coating is removed from the chamber,

wherein the above steps and transitions from one step to the next are performed under vacuum which is set by means of a protective gas,

wherein at least 99% of the intermediate layer is kept free of constituents initially contained in the substrate, and

wherein at least 99% of the intermediate layer is kept free of non-oxidised metals; and

wherein the substrate coating, consisting of the intermediate layer and the coating applied to it, has a layer thickness of 1 to 30 μm.

9. The substrate according to claim 8 , wherein the substrate coating is completely kept free of constituents initially contained in the substrate and the coating applied onto the intermediate layer is completely kept free of non-oxidised metals.

10. The substrate according to claim 8 , wherein the substrate is selected from a group comprising stainless steel and elements of the nickel group as well as coated stainless steel from elements of the nickel group.

11. The substrate according to claim 8 , wherein the coating applied onto the intermediate layer consists of ruthenium dioxide.

12. The substrate according to claim 8 , wherein the coating applied onto the intermediate layer is made up of a mixture of the metal oxides of ruthenium dioxide:iridium dioxide:titanium dioxide.

13. The substrate according to claim 8 , wherein the intermediate layer features uneven areas on its surface.

14. The substrate according to claim 8 , wherein the coating applied onto the intermediate layer features uneven areas on its surface.