Method for producing nanosurfaces with nano, micron, and/or submicron structures on a polymer
The present invention relates to a modified polymeric material. The modified polymeric material includes a polymer having a modified surface, where the modified surface includes nano, micron, and/or submicron scale features. The present invention also relates to an implant comprising the modified polymeric material. The present invention further relates to processes for making the modified polymeric material and the implant.
1. A process for preparing a modified polymeric material, said process comprising:
providing a polymer selected from the group consisting of polypropylene, polyetheretherketone (PEEK), poly lactic glycolic acid, poly lactic lactic acid, poly lactic acid, and polyurethane; and
subjecting the polymer to a high vacuum treatment regimen under conditions effective to modify the surface of the polymer by introducing nano, micron, and/or submicron scale features to the surface of the polymer,
wherein said high vacuum treatment regimen comprises simultaneously heating the polymer at a temperature of between about 275° C. and about 400° C. and incubating the polymer in a vacuum chamber under high vacuum conditions in a range of 10 −2 Torr to 10 −6 Torr effective to modify the surface of the polymer,
wherein said subjecting comprises:
(a) loading the polymer at a temperature of about 150° C.;
(b) applying high vacuum conditions of about 10 mTorr;
(c) increasing the temperature to about 350° C. over the course of about 1 hour;
(d) maintaining the polymer at about 350° C. at 10 mTorr for about 1 hour;
(e) decreasing the temperature to about 150° C. over the course of about 1 hour; and
(f) extracting the polymer at about 150° C.
2. The process according to claim 1 , wherein said incubating is carried out for at least 5 hours.
3. The process according to claim 1 further comprising:
storing the extracted polymer under high vacuum conditions in a range of 10 −2 Torr to 10 −6 Torr for about 8 hours.
4. The process according to claim 1 further comprising:
applying an acid etching procedure either before or after the polymer is modified; and/or
integrating/coating the modified polymeric material with hydroxyapatite, titanium, calcium phosphate, and/or the like to yield a two layer or integration of the modified polymeric material and the hydroxyapatite, titanium, calcium phosphate.
5. The process according to claim 1 , wherein the polymer is in the form of a polymeric film, fiber, sphere, ovoid, rod, filament, monofilament, or scaffold, plug, or matrix.
6. The process according to claim 1 , wherein said modified polymeric material is effective to modify biological response, fixation, or therapeutic attachment/delivery compared to a corresponding non-modified polymeric material.
7. The process according to claim 6 , wherein the biological response is selected from the group consisting of protein or antibody adsorption, cell attachment, cell function, and tissue growth.
8. The process according to claim 6 , wherein the therapeutic is selected from the group consisting of a peptide, protein, growth factor, antibody, drug, metal, antimicrobial metal, biologic tissue, biologic agent, chemical agent, stem cell, and modified cell.
9. The process according to claim 1 wherein the modified polymer comprises:
a functional attachment effective to increase biological response or therapeutic attachment/delivery; and/or
a ceramic, metal, or another polymer integrated into the modified polymeric material or coated onto the surface of the modified polymeric material.
10. The process according to claim 9 , wherein the functional attachment is selected from the group consisting of a peptide, protein, growth factor, antibody, drug, metal, antimicrobial metal, biologic tissue, biologic agent, chemical agent, stem cell, and modified cell.