Coated cutting tool, cutting member or wear part

1. A method of forming a coated cutting tool, cutting member or a wear part having a chemical vapor deposition (CVD) coating, comprising the steps of:

(a) providing a substrate selected from the group consisting of high speed steel alloys, carbon steels, low alloyed steels, austenitic stainless steels, ferritic stainless steels, martensitic stainless steels, tool steels, cemented carbides, nickel and cobalt super alloys, oxide ceramics and nitride ceramics;

(b) placing the substrate in a CVD reaction chamber, and

(c) depositing, by CVD, an alloyed coating layer comprising CVD reaction products of: (c1) a titanium chloride; (c2) chromium chloride and optionally one or more of a vanadium halide and a silicon halide; and (c3) one or more of nitrogen, hydrogen and methane, such that:

the alloyed coating layer has the general formula (Ti 100-a-b-c Cr a V b Si c )C x N y O z , where x+y+z=1, a+b+c>0, and a is between 0.1% and 30.0% of total metal content.

2. A method of forming a coated cutting tool, cutting member or a wear part having a chemical vapor deposition (CVD) coating, comprising the steps of:

(a) providing a substrate selected from the group consisting of high speed steel alloys, carbon steels, low alloyed steels, austenitic stainless steels, ferritic stainless steels, martensitic stainless steels, tool steels, cemented carbides, nickel and cobalt super alloys, oxide ceramics and nitride ceramics;

(b) placing the substrate in a CVD reaction chamber, and

(c) depositing, by CVD, an alloyed coating layer comprising CVD reaction products of: (c1) a titanium chloride; (c2) chromium chloride and optionally one or more of a vanadium halide and a silicon halide; and (c3) one or more of nitrogen, hydrogen and methane, such that:

the alloyed coating layer has the general formula (Ti 100-a-b-c Cr a V b Si c )C x N y O z , where x+y+z=1, a+b+c>0, and a is between 0.1% and 30.0% of total metal content; wherein

the titanium chloride, the chromium chloride, the optional vanadium halide and silicon halide, and the one or more of nitrogen, hydrogen and methane, are reacted at a temperature of between 720° C. and 1100° C.

3. The method of claim 2 , wherein the titanium chloride comprises titanium tetrachloride.

4. The method of claim 3 , wherein a ratio of partial pressure of the titanium tetrachloride to partial pressure of any one or more of the chromium chloride and the optional vanadium halide and silicon halide is between 1:1 and 99:1.

5. The method of claim 3 , wherein:

the alloyed coating layer comprises CVD reaction products of at least titanium tetrachloride, chromium chloride and one or more of nitrogen, hydrogen and methane; and

the partial pressure of chromium chloride is between 0.1% and 30% of total partial pressure of metal chloride in the CVD reaction chamber.

6. The method of claim 5 , wherein:

the alloyed coating layer comprises CVD reaction products of titanium tetrachloride, chromium chloride, nitrogen and hydrogen.

7. The method of claim 5 , wherein:

the alloyed coating layer comprises CVD reaction products of titanium tetrachloride, chromium chloride, nitrogen, methane and hydrogen.

8. The method of claim 5 , wherein:

the alloyed coating layer comprises CVD reaction products of titanium tetrachloride, chromium chloride, methane and hydrogen.

9. The method of claim 5 , wherein:

the alloyed coating layer comprises CVD reaction products of titanium tetrachloride, chromium chloride, methane, nitrogen, carbon dioxide and hydrogen.

10. The method of claim 5 , wherein:

the alloyed coating layer comprises CVD reaction products of titanium tetrachloride, chromium chloride, CH 3 CN, nitrogen and carbon dioxide.

11. The method of claim 2 , further comprising:

preparing the substrate by a process including at least one of degreasing, sandblasting and washing, prior to depositing the alloyed coating layer.

12. The method of claim 2 , further comprising:

depositing, with CVD, at least one layer each of TiN and MT-TiCN, prior to depositing the alloyed coating layer.

13. The method of claim 2 , further comprising:

depositing, with CVD, at least one coating layer onto the alloyed coating layer, after depositing the alloyed coating layer.

14. The method of claim 2 , wherein:

the alloyed coating layer comprises CVD reaction products of titanium tetrachloride, chromium chloride, nitrogen, methane and hydrogen;

x>0; and

y>0.

15. The method of claim 2 , wherein, in step (c), relative proportion of chromium to titanium in the CVD reaction chamber is at least 5%.

16. A coated cutting tool, cutting member or wear part made in accordance with the method of claim 1 .

17. A method of forming a coated cutting tool, cutting member or a wear part having a chemical vapor deposition (CVD) coating, comprising the steps of:

(a) providing a substrate selected from the group consisting of high speed steel alloys, carbon steels, low alloyed steels, austenitic stainless steels, ferritic stainless steels, martensitic stainless steels, tool steels, cemented carbides, nickel and cobalt super alloys, oxide ceramics and nitride ceramics;

(b) placing the substrate in a chemical vapor deposition reaction chamber, and

(c) depositing, by CVD, an alloyed coating layer of (Ti 100-a-b-c Cr a V b Si c )C x N y O z , where x+y+z=1, x>0, and a is between 0.1% and 30.0% of total metal content, wherein:

the CVD is carried out at a temperature in the range of 720° C. to 1100° C. by reacting a mixture of:

(i) titanium tetrachloride, chromium chloride and optionally one or more of vanadium chloride and silicon chloride;

(ii) either methane or CH 3 CN; and

(iii) at least one of nitrogen and hydrogen.

18. The method of claim 17 , further comprising:

depositing, with CVD, at least one layer each of TiN and MT-TiCN, prior to depositing the alloyed coating layer.

19. The method of claim 18 , wherein:

nitrogen is included in the mixture reacted in step (c);

x>0; and

y>0.

20. The method of claim 18 , wherein, in step (c), relative proportion of chromium to titanium in the CVD reaction chamber is at least 5%.

21. A coated cutting tool, cutting member or wear part made in accordance with the method of claim 17 .