Ultrathin surface coating on negative electrodes to prevent transition metal deposition and methods for making and use thereof
View Patent ↗An electrode material for use in an electrochemical cell, like a lithium-ion battery, is provided. The electrode material may be a negative electrode comprising graphite, silicon, silicon-alloys, or tin-alloys, for example. By avoiding deposition of transition metals, the battery substantially avoids charge capacity fade during operation. The surface coating is particularly useful with negative electrodes to minimize or prevent deposition of transition metals thereon in the electrochemical cell. The coating has a thickness of less than or equal to about 40 nm. Methods for making such materials and using such coatings to minimize transition metal deposition in electrochemical cells are likewise provided.
1. An electrode material for an electrochemical cell comprising:
a coating formed on exposed surface regions of a negative electrode comprising a material selected from the group consisting of: graphite, silicon, silicon-containing alloys, tin-containing alloys, and combinations thereof, wherein the coating has a thickness of less than or equal to about 40 nm to minimize or prevent deposition of transition metals so that less than or equal to about 5% of a surface area of the exposed surface regions of the negative electrode within the electrochemical cell has any transition metal deposited thereon.
2. The electrode material of claim 1 , wherein the coating is selected from the group consisting of: an oxide-based coating, a fluoride-based coating, and a nitride-based coating.
3. The electrode material of claim 1 , wherein the coating is an oxide-based surface coating selected from the group consisting of: aluminum oxide (Al 2 O 3 ), silicon dioxide (SiO 2 ), titanium oxide (TiO 2 ), zirconium oxide (ZrO 2 ), and zinc oxide (ZnO).
4. The electrode material of claim 1 , wherein the coating comprises aluminum oxide (Al 2 O 3 ) and the negative electrode comprises graphite.
5. The electrode material of claim 1 , wherein the thickness of the coating is greater than or equal to about 0.5 nm to less than or equal to about 15 nm.
6. A lithium-ion electrochemical cell comprising:
a negative electrode having a coating formed on exposed surface regions at a thickness of less than or equal to about 40 nm, wherein the negative electrode comprises a negative electroactive material selected from the group consisting of: graphite, silicon, silicon-containing alloys, tin-containing alloys, and combinations thereof;
a positive electrode comprising a positive electroactive material comprising a transition metal;
a separator; and
an electrolyte;
wherein the coating minimizes or prevents deposition of the transition metal on the negative electrode so that less than or equal to about 5% of a surface area of the exposed surface regions has any transition metal deposited thereon and the coating serves to maintain charge capacity within 20% of a target charge capacity of the lithium-ion electrochemical cell for greater than or equal to about 500 hours of operation.
7. The lithium-ion electrochemical cell of claim 6 , wherein the coating is selected from the group consisting of: an oxide-based coating, a fluoride-based coating, and a nitride-based coating.
8. The lithium-ion electrochemical cell of claim 6 , wherein the coating is an oxide-based coating having a thickness of less than or equal to about 20 nm.
9. The lithium-ion electrochemical cell of claim 6 , wherein the coating comprises aluminum oxide (Al 2 O 3 ) and the negative electroactive material comprises graphite.
10. The lithium-ion electrochemical cell of claim 6 , wherein the coating is an oxide-based surface coating selected from the group consisting of: aluminum oxide (Al 2 O 3 ), silicon dioxide (SiO 2 ), titanium oxide (TiO 2 ), zirconium oxide (ZrO 2 ), and zinc oxide (ZnO).
11. The lithium-ion electrochemical cell of claim 6 , wherein the transition metal is selected from the group consisting of: manganese (Mn), nickel (Ni), cobalt (Co), and combinations thereof.
12. The lithium-ion electrochemical cell of claim 6 , wherein the transition metal is manganese (Mn) and the positive electroactive material is selected from the group consisting of: lithium manganese oxide (Li (1+x) Mn (2−x) O 4 ), where 0≦x ≦1, lithium manganese nickel oxide (LiMn (2−x) Ni x O 4 ), where 0≦x ≦1, lithium nickel manganese cobalt oxide (Li(Ni x Mn y Co z )O 2 ), where 0≦x ≦1, 0≦y ≦1, 0 ≦z ≦1, and x+y+z=1, and combinations thereof.
13. A lithium-ion electrochemical cell comprising:
a pre-fabricated negative electrode comprising a negative electroactive material and a polymeric binder, wherein the negative electroactive material is selected from the group consisting of: graphite, silicon, silicon-containing alloys, tin-containing alloys, and combinations thereof;
a coating having a thickness of less than or equal to about 40 nm formed on exposed surface regions of the pre-fabricated negative electrode;
a positive electrode comprising a positive electroactive material comprising a transition metal;
a separator; and
an electrolyte; wherein the coating minimizes or prevents deposition of the transition metal on the pre-fabricated negative electrode so that less than or equal to about 5% of a surface area of the exposed surface regions has any transition metal deposited thereon and the coating serves to maintain charge capacity within 20% of a target charge capacity of the lithium-ion electrochemical cell for greater than or equal to about 500 hours of operation.
14. The electrode material of claim 1 , wherein the coating on the exposed surface regions is a conformal coating.
15. The lithium-ion electrochemical cell of claim 6 , wherein the coating on the exposed surface regions is a conformal coating.