Surface modification of battery materials and method for making a battery

1. A method of chemically modifying a surface of an electrochemically active component of a lithium ion battery, the method comprising:

(a) receiving the electrochemically active material for the lithium ion battery;

(b) fabricating a stack or a jelly roll containing the electrochemically active material after electrode drying; and

(c) following fabricating the stack or the jelly roll, exposing the electrochemically active material to a gaseous reactant under conditions that chemically modify surfaces of the electrochemically active material that are accessible to the gaseous reactant, and thereby produce a modified electrochemically active material having improved properties for use in the lithium battery, wherein the surface is modified to a depth of less than 5 nm.

2. The method of claim 1 , wherein the gaseous reactant has a molecular weight of about 300 g/mol or less.

3. The method of claim 1 , wherein the gaseous reactant is selected from the group consisting of hydrides, oxides, sulfides, oxysulfides, fluorides, and oxyfluorides of carbon, sulfur, phosphorus and boron.

4. The method of claim 1 , wherein the gaseous reactant is provided in a carrier gas chosen to affect the reactivity of the gaseous reactant with the electrochemically active material.

5. The method of claim 1 , wherein the gaseous reactant is selected from the group consisting of carbon dioxide (CO 2 ), carbon monoxide (CO), boron trifluoride (BF 3 ), carbon tetrafluoride (CF 4 ), carbonyl fluoride (COF 2 ), carbonyl sulfide (COS), fluoroform, forane, methyl fluoride, hexafluoropropylene, hydrogen sulfide, nitrogen trifluoride, phosphorus pentafluoride, perfluoropropane, sulfur dioxide, sulfur hexafluoride, sulfur tetrafluoride, and combinations thereof.

6. The method of claim 1 , wherein the gaseous reactant comprises a mixture of two or more of gaseous compounds.

7. The method of claim 6 , wherein one of the compounds is selected from the group consisting of nitrogen, helium, and argon.

8. The method of claim 1 , wherein the electrochemically active material is an anode active material, wherein the anode active material is a material that intercalates or inserts an alkali metal ion.

9. The method of claim 8 , wherein the anode active material is lithium titanium oxide.

10. The method of claim 8 , wherein the anode active material is silicon or silicon alloy.

11. The method of claim 1 , wherein the electrochemically active material is a cathode active material wherein the cathode active material is LiMO 2 , LiMPO 4 , LiM 2 O 4 , a lithium metal silicide, MS x (metal sulfide), or M x O y (metal oxide), where M is metal such as V, Mn, Fe, Co, Ni, Al, Si, or a combination thereof.

12. The method of claim 11 , wherein the cathode active material is a lithium metal oxide, lithium mixed metal oxide, lithium metal phosphate, or lithium mixed metal phosphate selected from the group consisting of LiCoO 2 , LiMnO 2 , LiNiO 2 , LiNi x Co 1−x O 2 , LiNi x Co y Mn (1−x−y) O 2 , LiNi x Co y Al (1−x−y )O 2 whereas 0<x<1, 0<y<1, LiFePO 4 , LiMnPO 4 , LiCoPO 4 , LiFe x Mn 1−x PO 4 , LiNi x Mn 1−x O 4 .

13. The method of claim 1 , further comprising drying the electrochemically active material prior to exposing the electrochemically active material to the gaseous reactant.

14. The method of claim 1 , further comprising contacting the stack or jellyroll with electrolyte after exposing the electrochemically active material to the gaseous reactant.

15. A method of chemically modifying a surface of an electrochemically active component of a lithium ion battery, the electrochemically active material being an anode active material and/or a cathode active material, the method comprising:

(a) receiving the electrochemically active material for the lithium ion battery;

(b) fabricating a stack or a jelly roll containing the electrochemically active material after electrode drying; and

(c) exposing the electrochemically active material to a gaseous reactant that removes surface carbonates and/or deactivates surface hydroxyl groups on the surface of the electrochemically active material.

16. The method of claim 15 , wherein receiving the electrochemically active material for the lithium ion battery further comprises receiving an active powder, an active powder mixed with conductive additives, or a coated electrode wherein the coated electrode is compressed or uncompressed.

17. The method of claim 15 , further comprising exposing the electrochemically active material to the gaseous reactant under conditions that chemically modify surfaces of the electrochemically active material that are accessible to the gaseous reactant, and thereby produce a modified electrochemically active surface wherein the surface is modified to a depth less than 5 nm.

18. The method of claim 15 , further comprising prior to exposing the electrochemically active material, fabricating a stack or a jelly roll containing the electrochemically active material.

19. A method of chemically modifying a surface of an electrochemically active component of a lithium ion battery, the method comprising:

(a) receiving the electrochemically active material for the lithium ion battery and fabricating a stack or a jelly roll containing the electrochemically active material; and

(b) exposing the electrochemically active material, after fabricating the stack or the jelly roll, to a gaseous oxidizing agent under conditions that chemically modify soluble metal ions present on surfaces of the electrochemically active material that are accessible to the gaseous oxidizing agent; and

(c) forming an insoluble metal salt of the metal ions on the surface of the electrochemically active material.

20. The method of claim 19 , wherein the gaseous oxidizing agent is fluorine and an insoluble metal fluoride is formed.

21. The method of claim 19 , wherein the soluble metal ion is one of Mn 2+ , Mn 3+ , Co 2+ , and Ni 2+ .

22. An electrochemical cell comprising:

a jelly roll or a stack comprising an anode, a cathode, and a separator;

wherein the jelly roll or the stack is exposed to a gaseous reactant that results in electrochemically active material surfaces to be free of hydroxyl groups; and

an electrolyte in contact with the electrochemically active material surfaces.

23. The electrochemical cell of claim 22 , wherein the electrochemically active material surfaces are covered by insoluble metal salts.