Welding a joint
View Patent ↗Methods for welding a joint are disclosed herein. One example of the method involves welding the joint between two workpieces. Energy is focused onto the joint to weld the joint. The focus of the energy moves relative to the joint. A vaporized material is displaced from a keyhole created by the welding. The vaporized material is vaporized by the energy. A pool of molten material is formed adjacent the keyhole during operation of the energy at the joint. The pool of molten material is manipulated by displacing a portion of the molten material from a near end of the pool and from lateral sides of the pool to a far end of the pool. The far end of the pool is distal to the near end.
1. A method of welding a joint between two workpieces, the method comprising:
focusing energy onto the joint to weld the joint, the focus of the energy moving relative to the joint;
vaporizing, by the energy, a zinc or magnesium constituent of any of the two workpieces;
directing a gas jet, separate from the source of energy, toward a keyhole created by the welding;
moving the zinc or magnesium vapor, using the gas jet, away from the keyhole;
forming a pool of molten material adjacent the keyhole during operation of the energy at the joint; and
pushing, using the gas jet, a portion of the molten material from a near end of the pool and from lateral sides of the pool to a far end of the pool, the far end being distal to the near end wherein the near end of the pool is an end that is closest to the keyhole.
2. The method as defined in claim 1 wherein the energy is chosen from a laser beam, an electron beam, and an arc.
3. The method as defined in claim 1 wherein the zinc or magnesium constituent has a lower boiling point than a melting point of a base material from which the any of the two workpieces is formed.
4. The method as defined in claim 1 wherein the gas jet is applied to the pool of molten material along a nozzle axis at an angle defined from a line parallel to a direction of the energy, the angle ranging from about 0 degrees to about 90 degrees.
5. The method as defined in claim 1 wherein the gas jet is applied to the pool of molten material along a flow axis coincident with a leading axis of the keyhole.
6. The method as defined in claim 1 wherein the gas jet is formed by a nozzle having an inlet orifice and an outlet orifice, the inlet orifice and the outlet orifice each having a respective equivalent diameter ranging from about 0.1 mm to about 200 mm.
7. The method as defined in claim 1 , further comprising applying the gas jet at a flow rate determined in response to a linear energy, a nozzle axis angle, a welding speed, a stand-off distance, or an energy angle.
8. The method as defined in claim 2 wherein the energy is a laser beam and the method further comprises applying a gas jet to displace a laser-induced plasma from the keyhole, the laser-induced plasma formed by ionization of material in the joint by the laser beam.
9. The method as defined in claim 3 wherein the zinc or magnesium constituent is a coating disposed on a surface of any of the two workpieces.
10. The method as defined in claim 5 wherein the gas jet is formed by a nozzle having a nozzle wall defining a cylindrical conduit with an axial length of about 26 mm from an inlet orifice of the nozzle to an outlet orifice of the nozzle.