Exhaust gas purifying catalyst and production method for same
Disclosed is an exhaust gas purifying catalyst which includes barium hexaaluminate, and palladium and barium which are supported on barium hexaaluminate, wherein the amount of supported palladium, as reduced to metallic Pd, is 0.2 to 3.5 mass % with respect to the mass of barium hexaaluminate; the amount of supported barium, as reduced to BaO, is 1 to 20 mass % with respect to the mass of barium hexaaluminate; and the ratio by mole of supported barium to supported palladium, Ba/Pd, is (0.5 to 10)/1; an exhaust gas purifying catalyst product which has a catalyst support made of a ceramic or metallic material, and a layer which is formed of the exhaust gas purifying catalyst as a predominant component and which is supported on the catalyst support; and a method for producing the exhaust gas purifying catalyst product.
1. An exhaust gas purifying catalyst, comprising barium hexaaluminate, and palladium and barium which are supported on barium hexaaluminate, wherein the amount of supported palladium, as reduced to metallic Pd, is 1.0 to 3.5 mass % with respect to the mass of barium hexaaluminate; the amount of supported barium, as reduced to BaO, is 2 to 15 mass % with respect to the mass of barium hexaaluminate; and the ratio by mole of supported barium to supported palladium, Ba/Pd, is (2 to 4.6)/1.
2. The exhaust gas purifying catalyst according to claim 1 , wherein the barium hexaaluminate is Ba x Al y O z , wherein x is 0.75 to 1, y is 10.9 to 12, and z is 17.14 to 19.
3. An exhaust gas purifying catalyst product, characterized by comprising a catalyst support made of a ceramic or metallic material, and a layer which is formed of an exhaust gas purifying catalyst as recited in claim 1 as a predominant component and which is supported on the catalyst support.
4. An exhaust gas purifying catalyst product, characterized by comprising a catalyst support made of a ceramic or metallic material, and a layer which is formed of an exhaust gas purifying catalyst as recited in claim 2 as a predominant component and which is supported on the catalyst support.
5. A method for producing an exhaust gas purifying catalyst product, compressing:
dispersing a barium hexaaluminate first slurry which has been subjected to wet grinding in an aqueous solution containing a water-soluble palladium compound and a water-soluble barium compound, to thereby form a second slurry, wherein the secondary slurry having the amount of supported palladium, as reduced to metallic Pd, is 1.0 to 3.5 mass % with respect to the mass of barium hexaaluminate; the amount of supported barium, as reduced to BaO, is 2 to 15 mass % with respect to the mass of barium hexaaluminate and the ratio by mole of supported barium to supported palladium, Ba/Pd, is (2 to 4.6)/1;
applying the second slurry onto a catalyst support made of a ceramic or metallic material; and
drying and firing the second slurry applied on the catalyst support.