Zeolite, manufacturing method of the same, and catalytic cracking batalyst of paraffin
Provided is a beta-type zeolite which has a high catalytic activity and is not easily deactivated. The beta-type zeolite of the invention has a substantially octahedral shape, has a Si/Al ratio of 5 or more, and is a proton-type zeolite. The Si/Al ratio is preferably 40 or more. This beta-type zeolite is preferably obtained by transforming a raw material beta-type zeolite synthesized without using a structure directing agent into an ammonium-type zeolite through ion exchange, then, exposing the beta-type zeolite to water vapor, and subjecting the exposed beta-type zeolite to an acid treatment.
1. A beta-type zeolite which has a substantially octahedral shape, has a Si/Al ratio of 14 or more, and is a proton-type zeolite.
2. The beta-type zeolite according to claim 1 ,
wherein the Si/Al ratio is 40 or more.
3. The beta-type zeolite according to claim 1 obtained by transforming a raw material beta-type zeolite synthesized without using a structure directing agent into an ammonium-type zeolite through ion exchange, then, exposing the beta-type zeolite to water vapor, and subjecting the exposed beta-type zeolite to an acid treatment.
4. A catalytic cracking catalyst of paraffin including the beta-type zeolite according to claim 1 .
5. A manufacturing method of a beta-type zeolite which has a substantially octahedral shape in which a raw material beta-type zeolite is transformed into an ammonium-type zeolite through ion exchange, then, exposed to water vapor, and subjected to an acid treatment, thereby obtaining the beta-type zeolite having a substantially octahedral shape and having an increased Si/Al ratio of 14 or more, wherein a beta-type zeolite synthesized without using a structure directing agent is used as the raw material beta-type zeolite to be ion-exchanged.
6. The manufacturing method according to claim 5 ,
wherein the ion-exchanged raw material beta-type zeolite is exposed to water vapor at 150° C. to 1000° C. for 1 hour to 48 hours.
7. The manufacturing method according to claim 5 ,
wherein the raw material beta-type zeolite which has been exposed to water vapor is subjected to an acid treatment at 40° C. to 100° C. for 1 hour to 24 hours using a mineral acid.
8. The manufacturing method according to claim 5 ,
wherein a beta-type zeolite having a Si/Al ratio of 40 or more is obtained.