Method of refining metal alloys A method of refining the grain size of (i) an alloy comprising aluminum and at least 3% w/w silicon or (ii) an alloy comprising magnesium, comprises the steps of (a) adding sufficient niobium and boron to the alloy in order to form niobium diboride or Al 3 Nb or both, or (b) adding niobium diboride to the alloy, or (c) adding Al 3 Nb to the alloy, or (d) any combination thereof.
1. A method of producing a masterbatch alloy for refining the grain size of a bulk alloy which is (i) an alloy comprising aluminium and at least 3% w/w silicon or (ii) an alloy comprising magnesium, comprising the step of:
(a) adding sufficient niobium and boron to a portion of an alloy comprising aluminum and at least 3% w/w silicon or (ii) an alloy comprising magnesium in order to form niobium diboride and Al 3 Nb, to refine the grain size of the alloy.
2. The method as claimed in claim 1 , wherein the alloy which is being refined comprises aluminium and silicon and wherein at least some of the niobium diboride reacts to form Al 3 Nb.
3. The method as claimed in claim 1 , wherein the alloy which is being refined comprises magnesium and aluminium.
4. The method as claimed in claim 1 , wherein the amount of niobium diboride is at least 0.001% by weight of the alloy.
5. The method as claimed in claim 1 , wherein said amount of niobium diboride is no more than 10% by weight of the alloy.
6. The method as claimed in claim 1 , wherein the alloy comprises aluminium and from 3 to 25 wt % silicon.