Method of forming polymeric foam and related foam articles
Methods of forming polymeric foams are provided. The methods may involve co-extruding a foam layer along with one or more skin layers. In some embodiments, the skin layer(s) may be removed (e.g., in a peeling operation); while, in other embodiments, the skin layer(s) may form part of the final article. The methods are particularly well suited for producing polymeric foams from polymeric materials that are considered to be difficult to foam by those of skill in the art.
1. A method comprising:
extruding a first stream and a second stream to form an annular extrudate, wherein the first stream comprises a single-phase solution of a first polymeric material comprising non-crosslinked polyether-block-amide and a blowing agent and the second stream comprises a second polymeric material, wherein the extrudate includes a foam layer comprising the first polymeric material comprising non-crosslinked polyether-block-amide and a skin layer comprising the second polymeric material, and wherein the first stream nucleates into said foam layer upon exiting an extrusion die inner passageway having an outward taper converging in a downstream direction approaching the die outlet;
blowing to expand the annular extrudate;
separating the foam layer from the skin layer of the expanded extrudate; and
collecting the separated foam layer, wherein the foam layer, after being collected, has a smooth surface and a plurality of cells having an average aspect ratio of less than 3:1 and an average maximum dimension of less than 200 microns, and wherein the collected foam layer comprises non-crosslinked polyether-block-amide and has a substantially closed cell structure.
2. The method of claim 1 , wherein said extruding further comprises co-extruding the first stream along with the second stream through the die to form the extrudate.
3. The method of claim 2 , further comprising co-extruding a third stream along with the first stream and the second stream, the third stream comprising a third polymeric material, and the extrudate further comprising a second skin layer comprising the third polymeric material.
4. The method of claim 1 , wherein the average maximum dimension of the cells is less than 150 microns.
5. The method of claim 1 , wherein the blowing agent is a physical blowing agent and the physical blowing agent is present in an amount less than about 2.5% by weight of the first stream.
6. The method of claim 1 , further comprising forming the single-phase solution in the extruder.
7. The method of claim 1 , wherein the die has an inner die wall that tapers outward approaching the die outlet at an angle of between 4° and 20° with respect to a centerline of the die.
8. The method of claim 1 , wherein the extrudate is further processed to form a sheet.
9. The method of claim 1 , wherein separating the foam layer from the skin layer occurs in the same processing line as the co-extrusion step.
10. The method of claim 1 , further comprising storing the extrudate including the foam layer and the skin layer prior to separating the foam layer from the skin layer.
11. The method of claim 1 , wherein the inner passageway of the extrusion die has a die gap converging to a dimension of less than or equal to 0.050 inch.
12. The method of claim 1 , wherein the inner passageway of the extrusion die has a die gap converging to a dimension of from at least 0.001 inch to less than or equal to 0.005 inch.
13. The method of claim 1 , wherein the foam layer has a density of between 0.3 g/cm 3 and 0.9 g/cm 3 .
14. The method of claim 1 , wherein the foam layer has a thickness variation of +/−8%.
15. The method of claim 1 , wherein the smooth foam layer surface is glossy.