Method for producing air bag base fabric, and air bag base fabric
A method for producing an air bag base fabric which has a silicone rubber coating layer on at least one surface of a substrate is provided. The silicone rubber coating layer is prepared by curing a liquid silicone rubber coating composition having the low viscosity required in the coating and excellent adhesion to the air bag base fabric. An air bag base fabric produced by this method is also provided. In this method, an air bag base fabric is produced by preliminarily treating at least one surface of the textile fabric with an organosilicon compound containing an epoxy group and an alkoxy group bonded to a silicon atom in one molecule to prepare a substrate fabric containing about 0.01 to 5 parts by weight of the organosilicon compound, and coating and curing the liquid silicone rubber coating composition of particular formulation on the substrate.
1. A method for producing an air bag base fabric comprising the steps of
preliminarily treating at least one surface of a textile fabric composed of a polyamide fiber with
(F) an organosilicon compound containing an epoxy group and an alkoxy group bonded to a silicon atom in one molecule
to prepare a substrate which is an air bag textile fabric composed of the polyamide fiber and containing 0.01 to 5 parts by weight of the organosilicon compound in relation to 100 parts by weight of the textile fabric before the treatment,
coating the at least one treated surface of the substrate with a liquid silicone rubber coating composition having a viscosity at 25° C. of up to 50 Pa·s comprising
(A) 100 parts by weight of an organopolysiloxane containing at least 2 alkenyl groups bonded to silicon atoms per molecule,
(B) an organohydrogenpolysiloxane containing at least 2 hydrogen atoms bonded to silicon atoms in one molecule at an amount such that the number of the hydrogen atoms bonded to the silicon atoms in this component is 1 to 10 per one alkenyl group bonded to the silicon atom in the component (A),
(C) an effective amount of an addition catalyst,
(D) 0 to 50 parts by weight of a fine powder silica having a specific surface area of at least 50 m 2 /g, and
(E) 0.01 to 5 parts by weight of an organometallic compound selected from titanium compounds and zirconium compounds,
but free of component (F), and
curing the composition to form a silicone rubber coating layer on at least one surface of the substrate.
2. A method for producing an air bag base fabric according to claim 1 , wherein the organosilicon compound (F) containing an epoxy group and an alkoxy group bonded to a silicon atom in one molecule is a silane or a cyclic or straight chain organosiloxane containing 2 to 120 silicon atoms and containing at least 1 epoxy group and at least 2 alkoxy groups bonded to the silicon atoms.
3. An air bag base fabric produced by the method of claim 1 , and having a silicone rubber coating layer formed by curing the liquid silicone rubber coating composition on at least one surface of the substrate comprising a textile fabric.
4. A method for producing an air bag base fabric according claim 1 , wherein the polyamide fiber is selected from 6,6 nylon and 6 nylon.
5. A method for producing an air bag base fabric according to claim 1 , wherein (D) the fine powder silica is a precipitated silica having an Na ion content in terms of Na 2 O of up to 0.35% by weight.